牵引销紧固螺钉断裂分析
Fracture Analysis of Fit Screws of a Tractor
摘 要
分析了牵引销紧固螺钉失效断裂的原因,对失效螺钉的化学成分、显微组织和裂纹及断口特征等进行了综合分析.结果表明：失效螺钉表层脱碳,在交变应力作用下,致螺纹齿根处疲劳损伤直至断裂.建议应严格控制热处理质量,避免脱碳;或以螺栓取代螺钉或将螺钉尺寸加大.
螺钉
疲劳
failure analysis
screw
fatigue
Abstract
The failure of fit screws used in a tractor was analyzed.A comprehensive study on composition,microstructure,fracture surfaces and cracks indicated that surface of screws underwent decarbonization,which led fatigue damnification at the root of the spiral burr and resulted in cracking.It is suggested to strictly control the quality of heat treatment to avoid decarbonization or substitute the screws with bolts or to use bigger screws.
中图分类号 U469.5
所属栏目
基金项目 广东省自然科学基金资助项目(04300026)
收稿日期 2005/1/4
修改稿日期 2005/3/28
网络出版日期
作者单位点击查看
备注陈灵(1971-),女,湖北房县人,工程师,硕士.
引用该论文: CHEN Ling,LIANG Si-zu,LIU Zheng-yi. Fracture Analysis of Fit Screws of a Tractor[J]. Materials for mechancial engineering, 2006, 30(4): 86～88
陈灵,梁思祖,刘正义. 牵引销紧固螺钉断裂分析[J]. 机械工程材料, 2006, 30(4): 86～88
被引情况:
【1】汪文瀚,何毅,诸葛宇明,金玉静, "SWRCH22A十字头螺钉断裂分析",理化检验－物理分册 47, 713-716(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB 3077-1978,合金结构钢号及化学成分[S].
【2】刘正义,吴连生,许麟康,等.机械装备失效分析图谱[M].广州:广东科技出版社,1990.
【3】GB/T 3098.1-2000,紧固机件机械性能 螺栓,螺钉,螺柱[S].
【4】周永欣,吕振林,张 敏,等.30CrMo钢泵体开裂失效分析[J].机械工程材料,2004,28(9):52-54.
【5】机械工程手册电机工程手册编辑委员会.机械工程手册:机械零部件设计卷[M].北京:机械工业出版社,1996.
【2】刘正义,吴连生,许麟康,等.机械装备失效分析图谱[M].广州:广东科技出版社,1990.
【3】GB/T 3098.1-2000,紧固机件机械性能 螺栓,螺钉,螺柱[S].
【4】周永欣,吕振林,张 敏,等.30CrMo钢泵体开裂失效分析[J].机械工程材料,2004,28(9):52-54.
【5】机械工程手册电机工程手册编辑委员会.机械工程手册:机械零部件设计卷[M].北京:机械工业出版社,1996.
相关信息