船用柴油机活塞连接螺栓断裂失效分析
Fracture Failure Analyses of Piston Connecting Bolt of Diesel Engine for Ship
摘 要
采用光学显微镜、扫描电镜和能谱分析等检测手段对船用柴油机活塞头和活塞裙的连接螺栓断裂原因进行了分析.结果表明：该连接螺栓的断裂属多疲劳源引起的疲劳断裂,疲劳源均位于螺纹牙根表面,是由车削螺纹表面加工精度不高而引起的;此外,显微组织中网状、块状铁素体的存在以及螺纹表层脱碳使连接螺栓疲劳强度下降也是造成断裂的重要原因.
连接螺栓
疲劳断裂
表面缺陷
failure analysis
connecting bolt
fatigue fracture
surface defect
Abstract
The fracture reasons of connecting bolt of piston head and piston skirt in a diesel engine for ship were analyzed by OM,SEM and EDS etc.The connecting bolt was fractured by fatigue with many fatigue sources,which entirely located at the fang surface of screw threads and resulted from the low surface machining precision of screw threads.The existence of reticulation and mass shape ferrite,decarbonization at the screw thread surface layer which induced decline of fatigue strength of connecting bolt were also the important reasons of fracture.
中图分类号 TG142
所属栏目
基金项目
收稿日期 2004/12/21
修改稿日期 2005/3/8
网络出版日期
作者单位点击查看
备注王国阳(1981-),男,河南洛阳人,硕士研究生.
引用该论文: WANG Guo-yang,XU Wei-ping,ZHANG Bao-qi,WANG De-he. Fracture Failure Analyses of Piston Connecting Bolt of Diesel Engine for Ship[J]. Materials for mechancial engineering, 2006, 30(4): 92～94
王国阳,徐卫平,张保奇,王德和. 船用柴油机活塞连接螺栓断裂失效分析[J]. 机械工程材料, 2006, 30(4): 92～94
被引情况:
【1】崔正强,吾之英,汪德健,李 强, "循环水泵泵轴联轴器螺栓断裂分析",理化检验－物理分册 46, 406-408(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】亨利G,豪斯特曼D.宏观断口学及显微断口学[M].北京:机械工业出版社,1990.
【2】任颂赞,张静如,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社,2003.
【3】布鲁克斯·查利R,阿肖克·考霍莱.工程材料的失效分析[M].北京:机械工业出版社,2003.
【4】熊琳,刘锦.船用柴油机设计手册(五)[M].北京:国防工业出版社,1982.
【5】王伯琴,陈录如,陈先锋,等.高强度螺栓连接[M].北京:冶金工业出版社,1991.
【2】任颂赞,张静如,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社,2003.
【3】布鲁克斯·查利R,阿肖克·考霍莱.工程材料的失效分析[M].北京:机械工业出版社,2003.
【4】熊琳,刘锦.船用柴油机设计手册(五)[M].北京:国防工业出版社,1982.
【5】王伯琴,陈录如,陈先锋,等.高强度螺栓连接[M].北京:冶金工业出版社,1991.
相关信息