氧化锌晶须填充尼龙1010复合材料的摩擦磨损性能
Sliding Tribological Behavior of Polyamide 1010 Composites Filled with ZnO Whisker
摘 要
采用模具挤压成型的方法制备了氧化锌晶须填充尼龙1010复合材料,使用纳米力学测试系统测试了不同含量氧化锌晶须复合材料的硬度和弹性模量,在UMT试验机上考察了复合材料的摩擦磨损性能,然后对磨损表面进行了SEM观察.结果表明：复合材料的硬度和弹性模量随氧化锌晶须含量的增加而增大;ZnOw在保持尼龙1010摩擦性能的同时,可使其耐磨性能提高60%左右.纯尼龙的主要磨损机制为粘着磨损和熔融,填充ZnOw后复合材料的磨损机制转变为疲劳剥层.
ZnO晶须
摩擦磨损
磨损机理
PA1010
ZnO whisker(ZnOw)
friction and wear
wear mechanism
Abstract
PA1010 composites filled with micrometer ZnO whiskers (ZnOw) were prepared by hot squeeze method.The nanohardness and elastic modulus of the composites were determined through nanoindentation on a triboindenter system.The sliding friction and wear behaviors were examined with a universal micro-tribometer in dry condition.The nanohardness and elastic modulus of the composites increased with the increasing content of ZnOw.The wear resistance of the composites was increased by about 60%,the friction property was maintained.The adhesion and melting were the main wear mechanism of pure PA1010,while wear mechanism of PA1010 composites shifted to fatigue rupture.
中图分类号 TH117.1 TQ334
所属栏目
基金项目 国家杰出青年基金资助项目(50225519);高等学校优秀青年教师教学科研奖励计划资助项目;江苏省高新技术转化基金资助项目
收稿日期 2005/3/7
修改稿日期 2005/5/20
网络出版日期
作者单位点击查看
备注王世博(1979-),男,河北邢台人,博士研究生.
引用该论文: WANG Shi-bo,GE Shi-rong,WANG Qing-liang,JIANG Zhi-min. Sliding Tribological Behavior of Polyamide 1010 Composites Filled with ZnO Whisker[J]. Materials for mechancial engineering, 2006, 30(5): 72～74
王世博,葛世荣,王庆良,姜志民. 氧化锌晶须填充尼龙1010复合材料的摩擦磨损性能[J]. 机械工程材料, 2006, 30(5): 72～74
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张文,陈长永,金增平,等.氧化锌晶/环氧树脂复合材料减振性能[J].青岛化工学院学报,1998,19(4):361-364.
【2】周柞万,谢宁,易锦.PVC/ZnOw复合材料的抗静电性能[J].西南交通大学学报,1998,33(2):179-182.
【3】吴华武,黄红花.含四针状ZnO晶须的高分子导电膜的研制[J].功能材料,1999,30(4):389-391.
【4】田雅娟,杨东梅,陈尔凡.四脚状氧化锌晶须增强尼龙6复合材料的研究[J].塑料工业,2002,30(5):32-34.
【5】品云阳.无机化学丛书[M].北京:科学出版社,1995.
【6】周柞万,彭卫明,客绍瑛.ZnO晶须及其树脂基复合材料的研究进展[J].材料导报,1999,19(3):57-59.
【7】周柞万,楚珑晟,顾利霞.ZnOw改善橡胶和轮胎耐磨性能的研究[J].汽车技术,2003,(7):29-32.
【8】Maloto W,Haruchiyo Y.The friction and wear properties of nylon[J].Wear,1986,110:379-388.
【2】周柞万,谢宁,易锦.PVC/ZnOw复合材料的抗静电性能[J].西南交通大学学报,1998,33(2):179-182.
【3】吴华武,黄红花.含四针状ZnO晶须的高分子导电膜的研制[J].功能材料,1999,30(4):389-391.
【4】田雅娟,杨东梅,陈尔凡.四脚状氧化锌晶须增强尼龙6复合材料的研究[J].塑料工业,2002,30(5):32-34.
【5】品云阳.无机化学丛书[M].北京:科学出版社,1995.
【6】周柞万,彭卫明,客绍瑛.ZnO晶须及其树脂基复合材料的研究进展[J].材料导报,1999,19(3):57-59.
【7】周柞万,楚珑晟,顾利霞.ZnOw改善橡胶和轮胎耐磨性能的研究[J].汽车技术,2003,(7):29-32.
【8】Maloto W,Haruchiyo Y.The friction and wear properties of nylon[J].Wear,1986,110:379-388.
相关信息