Effect of Rare Earth Element Cerium on Properties and Microstructure of Hot Dip Aluminum Coating on Q235 Steel
摘 要
研究了稀土铈对热浸镀铝层组织结构、耐蚀和耐热性能的影响.结果表明:稀土铈质量分数低于0.3%时,热浸镀铝层的耐蚀性能和高温抗氧化性能都得到提高,超过此含量镀层的性能下降.稀土铈使得过渡层由锯齿形结构转变为平滑结构,使镀层中FeAl3析出相在表层中呈网状分布,随其含量增加过渡层厚度减小.稀土含量超过0.3%时,稀土化合物在表层中呈条块状第二相析出并偏聚,并且随着稀土铈含量增加,表面层中稀土化合物呈块状,且偏聚程度加大.
Abstract
The effect of rare earth element Ce on the microstructure of hot dip aluminum(HDA) coating on Q235 steel have been studied by means of SEM and XRD.The anticorrosive property and oxidation resistance of the coating was also studied by immersion test in 3.5% sodium chloride solution and at 900 ℃ for 300 h respectively.If the content of Ce in the hot dip aluminum bath was lowere than 0.3%,with increasing the content of Ce in the bath,the anticorrosive property and oxidation resistance of HDA coating were improved obviously.If the content of Ce in the bath was higher than 0.3%,the properties of the HDA coating became poor.By adding Ce into the HDA bath,the saw-toothed shape of transition layer of HAD coating became smooth,FeAl3 phase distributed in the surface layer in netted shape,but the thickness of the transition layer varied little with increasing the content of Ce in the bath.If the content of Ce was more than 0.3% in the bath,the Ce compound separated out in strip-like shape in the surface layer and got together in the boundary of FeAl3 phase,and with increasing the Ce content in the bath,the shape of Ce compound became blocky and the degree of segregation was more serious.
中图分类号 TG178
所属栏目
基金项目 国家自然科学基金资助项目(50071066)
收稿日期 2005/5/7
修改稿日期 2005/7/30
网络出版日期
作者单位点击查看
备注于升学(1964-),男,黑龙江拜泉人,副教授,博士研究生.
引用该论文: YU Sheng-xue,XIA Yuan,YAO Mei. Effect of Rare Earth Element Cerium on Properties and Microstructure of Hot Dip Aluminum Coating on Q235 Steel[J]. Materials for mechancial engineering, 2006, 30(6): 77~79
于升学,夏原,姚枚. 稀土铈对热浸镀铝层组织和性能的影响[J]. 机械工程材料, 2006, 30(6): 77~79
被引情况:
【1】王友彬,曾建民, "钢板表面热浸镀锌层的拉伸断裂机理",机械工程材料 39, 13-17(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李华飞,俞敦义,郑家焱.热浸镀铝钢的性能及用途[J].材料保护,2001,34(5):21-23.
【2】顾文桂,钱卫江.热浸镀铝钢带镀层与合金层的组织结构[J].钢铁研究学报,1995,7(3):45-50.
【3】李国喜.钢材热浸镀铝工艺的研究与应用[J].材料保护,1993,25(9):13-16.
【4】陈军.热浸镀铝件高温抗氧化性能的研究[J].金属热处理,1999,(2):16-19.
【5】孙成伟.稀土在铝合金中的行为[M].北京:兵器工业出版社,1992.
【6】吴元康.含稀土抗氧化剂的热浸镀铝工艺研究[J].材料科学与工艺,1994,2(4):96-99.
【7】付瑞峰,徐滨士,马世宁,等.稀土元素对Al、Al合金线材电弧喷涂层的耐腐蚀性能试验[J].表面工程,1997,(4):36-40.
【2】顾文桂,钱卫江.热浸镀铝钢带镀层与合金层的组织结构[J].钢铁研究学报,1995,7(3):45-50.
【3】李国喜.钢材热浸镀铝工艺的研究与应用[J].材料保护,1993,25(9):13-16.
【4】陈军.热浸镀铝件高温抗氧化性能的研究[J].金属热处理,1999,(2):16-19.
【5】孙成伟.稀土在铝合金中的行为[M].北京:兵器工业出版社,1992.
【6】吴元康.含稀土抗氧化剂的热浸镀铝工艺研究[J].材料科学与工艺,1994,2(4):96-99.
【7】付瑞峰,徐滨士,马世宁,等.稀土元素对Al、Al合金线材电弧喷涂层的耐腐蚀性能试验[J].表面工程,1997,(4):36-40.
相关信息