Process Optimization of NiCrAlCo-Y2O3 Coating on an Aluminum Substrate by Plasma Spraying
摘 要
对喷涂距离、电流、主气流量和辅气流量四个等离子喷涂主要参数设计了四因素三水平的正交试验,研究了工艺参数对在铝基体上喷涂NiCrAlCo-Y2O3涂层的结合强度的影响,并对工艺优化前后的涂层性能进行了分析.结果表明:影响涂层与铝基体结合强度的因素主次顺序是电流、喷涂距离、主气流量和辅气流量;工艺优化后涂层的最大结合强度达到55.1 MPa.
Abstract
Orthogonal tests of spraying distance,electrical current,primary gas flow rate and secondary gas flow rate were carried in order to obtain an optimized plasma spraying parameters.The influence of spraying process parameters on bonding strength of NiCrAlCo-Y2O3 coating was investigated.And microstructure,microhardness and porosity of the coatings of before and after process optimization were studied.The results show that the electrical current and spraying distance have more effect on the bonding strength of the coating and aluminum substrate.An optimized process is achieved,and the bonding strength of optimized coating is improved to 55.1 MPa.
中图分类号 TG174.442
所属栏目
基金项目
收稿日期 2005/10/12
修改稿日期 2005/12/21
网络出版日期
作者单位点击查看
备注方学锋(1982-),男,安徽安庆人,硕士研究生.
引用该论文: FANG Xue-feng,WANG Ze-hua,XIA Zhi-min,LIU Teng-bin,LU Jie. Process Optimization of NiCrAlCo-Y2O3 Coating on an Aluminum Substrate by Plasma Spraying[J]. Materials for mechancial engineering, 2006, 30(11): 7~9
方学锋,王泽华,夏志敏,刘腾彬,陆婕. 铝基体等离子喷涂NiCrAlCo-Y2O3涂层工艺的优化[J]. 机械工程材料, 2006, 30(11): 7~9
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邢世凯,李聚霞,吴立勋,等.金属-陶瓷梯度功能材料在能燃机上的应用研究[J].机械工程材料,2005,29(5):61-63.
【2】谭昌瑶,王钧石.实用表面工程技术[M].北京:新时代出版社,1998.
【3】Luthra K L,Briant C L.Mechanism of adhesion of alumina on MCrAlY alloys[J].Oxid Met,1986,26:397-401.
【4】邓世均.高性能陶瓷涂层[M].北京:化学工业出版社,2004.
【5】Martin Friisa Christer Perssona,Jan Wigrenb.Influence of particle in-flight characteristics on the microstructure of atmospheric plasma sprayed yttria stabilized ZrO2[J].Surface and Coatings Technology,2001,(4):115-127.
【6】王 娜,王全胜,王富耻.等离子喷涂ZrO2热障涂层工艺参数优化设计[J].中国表面工程,2004,(3):13-16.
【7】徐仲安,王天保,李常英,等.正交试验设计法简介[J].科技情报开发与经济,2002,12(5):148-150.
【8】戴达煌,周克崧,袁镇海,等.现代材料表面技术科学[M].北京:冶金工业出版社,2004.
【2】谭昌瑶,王钧石.实用表面工程技术[M].北京:新时代出版社,1998.
【3】Luthra K L,Briant C L.Mechanism of adhesion of alumina on MCrAlY alloys[J].Oxid Met,1986,26:397-401.
【4】邓世均.高性能陶瓷涂层[M].北京:化学工业出版社,2004.
【5】Martin Friisa Christer Perssona,Jan Wigrenb.Influence of particle in-flight characteristics on the microstructure of atmospheric plasma sprayed yttria stabilized ZrO2[J].Surface and Coatings Technology,2001,(4):115-127.
【6】王 娜,王全胜,王富耻.等离子喷涂ZrO2热障涂层工艺参数优化设计[J].中国表面工程,2004,(3):13-16.
【7】徐仲安,王天保,李常英,等.正交试验设计法简介[J].科技情报开发与经济,2002,12(5):148-150.
【8】戴达煌,周克崧,袁镇海,等.现代材料表面技术科学[M].北京:冶金工业出版社,2004.
相关信息