采用喷撒工艺制备铁基粉末冶金摩擦材料
Preparation of Powder Metallurgy Iron-based Friction Materials by Sprinkling Powder Process
摘 要
研究了喷撒工艺在45钢基体上制备铁基粉末冶金摩擦材料的压制、烧结工艺,分析了工艺参数对铁基粉末冶金摩擦材料性能的影响,对摩擦层与钢板结合强度进行了重点分析.结果表明：试验条件下的最佳生产工艺的预烧结温度1 050 ℃,保温时间2 h,压制压力500 MPa,终烧结温度1 030 ℃,保温时间2 h,在此条件下,试样具有较高的硬度、适宜的密度及良好的结合强度.
粉末冶金
摩擦材料
结合强度
sprinkling powder process
powder metallurgy
friction material
bond strength
Abstract
Powder metallurgy iron-based friction materials were prepared on 45# steel by sprinkling powder process.The effect of parameters of compacting and sintering process on the properties of these materials were investigated and the bond strength between friction material and steel-backing was mainly studied.The optimization of process parameters is pre-sintered at 1 050 ℃ for 2 h,pressed by 500 MPa,then sintered at 1 030 ℃ for 2 h,the sample showed high hardness,suitable density and good bond strength.
中图分类号 TF125.9
所属栏目
基金项目
收稿日期 2006/1/5
修改稿日期 2006/3/5
网络出版日期
作者单位点击查看
备注海坤(1980-),男,辽宁阜新人,硕士研究生.
引用该论文: HAI Kun,HU Xue-sheng,GUO Shi-ju. Preparation of Powder Metallurgy Iron-based Friction Materials by Sprinkling Powder Process[J]. Materials for mechancial engineering, 2007, 31(1): 35～37
海坤,胡学晟,果世驹. 采用喷撒工艺制备铁基粉末冶金摩擦材料[J]. 机械工程材料, 2007, 31(1): 35～37
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李绍忠,贺奉嘉,黄伯云.浅析汽车摩擦材料现状与发展趋势[J].汽车技术,1995(3):50-55.
【2】曲在纲,黄月初.粉末冶金摩擦材料[M].北京:冶金工业出版社,2005:127-130.
【3】钟志刚,邓海金,李明,等.铜基金属陶瓷摩擦材料与钢背的结合强度研究[J].粉末冶金技术,2002(3):158-161.
【2】曲在纲,黄月初.粉末冶金摩擦材料[M].北京:冶金工业出版社,2005:127-130.
【3】钟志刚,邓海金,李明,等.铜基金属陶瓷摩擦材料与钢背的结合强度研究[J].粉末冶金技术,2002(3):158-161.
相关信息