Fabrication of Alumina/Diopside Composites by Hot-pressing Sintering Process
摘 要
采用热压烧结法制备了氧化铝/透辉石复相陶瓷材料,分析了复合材料的微观结构,测试了复合材料的断裂韧度、硬度和抗弯强度与透辉石颗粒含量的对应关系.结果表明:在28 MPa、1 450 ℃×30 min条件下热压烧结制备的复相陶瓷材料,其抗弯强度、断裂韧度均有明显提高,最高达到442.5 MPa和4.76 MPa·m1/2.
Abstract
Al2O3/diopside composites were fabricated by hot-pressing sintering process.Microstructure of the composites was analysed and mechanical properties such as fracture toughness,hardness and bending strength of the composites were tested.The bending strength and fracture toughness of alumina matrix ceramic composites sintered at 1 450 ℃,under 28 MPa for 30 min,are significantly improved and reache their maximums value of 4425 MPa and 4.76 MPa·m1/2,respectively.
中图分类号 TQ174
所属栏目
基金项目 山东省优秀中青年科学家科研奖励基金资助项目(2005BS04008)
收稿日期 2005/12/22
修改稿日期 2006/3/30
网络出版日期
作者单位点击查看
备注张希华(1965-),男,山东平原人,副研究员,博士后.
引用该论文: ZHANG Xi-hua,LIU Chang-xia,LI Mu-sen,ZHANG Jian-hua. Fabrication of Alumina/Diopside Composites by Hot-pressing Sintering Process[J]. Materials for mechancial engineering, 2007, 31(1): 38~40
张希华,刘长霞,李木森,张建华. 热压烧结法制备氧化铝/透辉石陶瓷复合材料[J]. 机械工程材料, 2007, 31(1): 38~40
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】林营,杨海波,王芬.直接金属氧化法制备SiCp/Al2O3-Al复合材料[J].机械工程材料,2005,29(6):27-29.
【2】ANYA C C.Microstructural nature of strengthening and toughening in Al2O3-SiC (p) nanocomposites[J].Journal of Materials Science,1999,34:5557-5567.
【3】邓建新,艾兴.SiC晶须增韧Al2O3陶瓷组成及其断裂行为的研究[J].材料科学与工程,1995,13(1):33-36.
【4】Tekeli S.High temperature ductility and cavitation behaviour of hot isostatically pressed (HIP)ZrO2/ Al2O3 composite containing 40 wt% Al2O3[J].Ceramics International,2003,29(2):169-174.
【5】Jayaseelan,Doni Nishikawa,Tadahiro Awaji,et al.Pressureless sintering of sol-gel derived alumina-zirconia composites[J].Materials Science and Engineering A,1998,256(1/2):265-270.
【6】赵永红,李光新,马新沛.MgO-Al2O3-SiO2系高强度微晶玻璃的晶化行为与力学性能[J].硅酸盐学报,2003,31(4):413-416.
【7】卡恩R W,哈森 P,克雷默 E J.材料科学与技术丛书(第11卷)——陶瓷的结构与性能[M].北京:科学出版社,1998.
【8】Sathiyakumar M,Gnanam F D.Role of wollastonite additive on density,microstructure and mechanical properties of alumina[J].Ceramics International,2003,29(8):869-873.
【2】ANYA C C.Microstructural nature of strengthening and toughening in Al2O3-SiC (p) nanocomposites[J].Journal of Materials Science,1999,34:5557-5567.
【3】邓建新,艾兴.SiC晶须增韧Al2O3陶瓷组成及其断裂行为的研究[J].材料科学与工程,1995,13(1):33-36.
【4】Tekeli S.High temperature ductility and cavitation behaviour of hot isostatically pressed (HIP)ZrO2/ Al2O3 composite containing 40 wt% Al2O3[J].Ceramics International,2003,29(2):169-174.
【5】Jayaseelan,Doni Nishikawa,Tadahiro Awaji,et al.Pressureless sintering of sol-gel derived alumina-zirconia composites[J].Materials Science and Engineering A,1998,256(1/2):265-270.
【6】赵永红,李光新,马新沛.MgO-Al2O3-SiO2系高强度微晶玻璃的晶化行为与力学性能[J].硅酸盐学报,2003,31(4):413-416.
【7】卡恩R W,哈森 P,克雷默 E J.材料科学与技术丛书(第11卷)——陶瓷的结构与性能[M].北京:科学出版社,1998.
【8】Sathiyakumar M,Gnanam F D.Role of wollastonite additive on density,microstructure and mechanical properties of alumina[J].Ceramics International,2003,29(8):869-873.
相关信息