不锈钢链板开裂原因分析
Cracking Analysis on Stainless Steel Chain Board
摘 要
对302不锈钢制链条链板失效件进行了分析.结果表明:原材料固溶处理温度偏低,未溶碳化物沿晶界分布,加之链条工作环境中存在大量的腐蚀性介质,从而导致链条产生晶间腐蚀,开裂系链条受到拉伸和其本身存在的冷加工残余应力所致.
链板
晶间腐蚀
奥氏体
stainless steel
chain board
intergranular corrosion
austenite
Abstract
The failure of 302 stainless steel chain board was analyzed.The results show the cracking reason is intergranular corrosion.Low solution treatment temperature of the raw material led to carbide not dissolving and distributing along the grain boundary.At the same time,working atmosphere of the chain board has a lot of corrosion medium.The tensile stress from using process and the residual stress from cold working process cause the cracking.
中图分类号 TH132.45
所属栏目
基金项目
收稿日期 2005/11/10
修改稿日期 2006/1/9
网络出版日期
作者单位点击查看
备注王荣(1966-),男,陕西洛南人,高级工程师,学士.
引用该论文: WANG Rong,LI Ling. Cracking Analysis on Stainless Steel Chain Board[J]. Materials for mechancial engineering, 2007, 31(1): 57～59
王荣,李玲. 不锈钢链板开裂原因分析[J]. 机械工程材料, 2007, 31(1): 57～59
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】安继儒,袁金华,雷群.中外常用金属材料手册[M].西安:陕西科学技术出版社,1998.
【2】任赞颂,张静江,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社,2003.
【3】沈松泉,黄振仁,顾彦成,等.压力管道安全技术[M].南京:东南大学出版社,1984.
【4】王磊.不锈钢管板裂纹成因分析[J].化工装备技术,2004,25(6):63-65.
【5】小若正化.金属的腐蚀破坏与防腐技术[M].北京:化学工业出版社,1988.
【2】任赞颂,张静江,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社,2003.
【3】沈松泉,黄振仁,顾彦成,等.压力管道安全技术[M].南京:东南大学出版社,1984.
【4】王磊.不锈钢管板裂纹成因分析[J].化工装备技术,2004,25(6):63-65.
【5】小若正化.金属的腐蚀破坏与防腐技术[M].北京:化学工业出版社,1988.
相关信息