膨胀干燥机加热夹套开裂原因分析
Cracking Analyses of Heating Jacket in Extruder-dryer
摘 要
膨胀干燥机加热夹套在实际使用中经常发生开裂事故,为了保证其正常运行,对加热夹套的开裂原因进行了分析.结果表明:加热夹套开裂的主要原因是316L奥氏体不锈钢不耐氯化物腐蚀,焊缝有一定的缺陷和腐蚀介质存在,属于一种典型的应力腐蚀失效形式.并探讨了防止其开裂的方法.
加热夹套
316L奥氏体不锈钢
应力腐蚀
extruder-dryer
heating jacket
316L austenitic stainless steel
stress corrosion cracking
Abstract
Cracking often takes place in heating jacket of extruder-dryer.The failure analysis of the heating jacket indicates that the austenitic stainless steel 316L is susceptible to stress corrosion cracking under the combined action of chloride environment and residual stresses induced by welding.An attempt to find an alternative material with better resistance to stress corrosion cracking was also discussed.
中图分类号 TQ050.9
所属栏目
基金项目
收稿日期 2006/2/15
修改稿日期 2006/4/29
网络出版日期
作者单位点击查看
备注唐世华(1971-),男,山东单县人,副研究员,博士.
引用该论文: TANG Shi-hua,HAO Jun-wen,PAN Hong-liang,CHEN Jue,WANG Shui-he. Cracking Analyses of Heating Jacket in Extruder-dryer[J]. Materials for mechancial engineering, 2007, 31(1): 63～66
唐世华,郝俊文,潘红良,陈珏,王水河. 膨胀干燥机加热夹套开裂原因分析[J]. 机械工程材料, 2007, 31(1): 63～66
被引情况:
【1】刘淑梅, "洗衣机不锈钢滚桶开裂失效分析",机械工程材料 33, 90-92(2009)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】潘红良,汤建华,黄五星,等.螺旋叶堆焊层脱落的原因分析及预防措施研究[J].机械工程材料,2004,28(6):51-54.
【2】潘红良,唐世华,黄五星.膨胀干燥机螺杆轴断裂失效分析[J].机械工程材料,2005,29(10):56-59.
【3】Pan H L,Tang S H,Hao J W.Failure analysis of a rotating cantilever shaft in chloride corrosive environment[J].Engineering Failure Analysis,2006,13(4):646-655.
【4】薛锦.应力腐蚀与环境氢脆[M].西安:西安交通大学出版社,1991.
【5】王莺,高增梁,张芳,等.316L钢高温疲劳裂纹扩展的规律研究[J].化工设备与管道,2005,42(2):49-51.
【6】许航,彭人民.奥氏体不锈钢发酵罐应力腐蚀裂纹探讨[J].机电技术,2003(2):36-39.
【7】Kasiviswanathan K V,Muralidharan N G,Raghu N,et al.Corrosion related failure of austenitic stainless steel components[C]//Corrosion of austenitic stainless steels.India:Narosa Publishing House,2002.
【8】刘正东,张国福.奥氏体不锈钢炉体应力腐蚀破裂失效分析[J].当代化工,2004,33(6):357-360.
【9】宋义全,武俊伟,李晓刚,等.常压塔顶316L不锈钢换热器管束的腐蚀失效分析[J].腐蚀科学与防护技术,2004,16(5):334-336.
【10】刘志盈.抗应力腐蚀开裂的选材标准化问题探讨[J].航天标准化,2005(4):39-42.
【11】钢制压力容器(二、相关标准)[M].北京:学苑出版社,1989.
【2】潘红良,唐世华,黄五星.膨胀干燥机螺杆轴断裂失效分析[J].机械工程材料,2005,29(10):56-59.
【3】Pan H L,Tang S H,Hao J W.Failure analysis of a rotating cantilever shaft in chloride corrosive environment[J].Engineering Failure Analysis,2006,13(4):646-655.
【4】薛锦.应力腐蚀与环境氢脆[M].西安:西安交通大学出版社,1991.
【5】王莺,高增梁,张芳,等.316L钢高温疲劳裂纹扩展的规律研究[J].化工设备与管道,2005,42(2):49-51.
【6】许航,彭人民.奥氏体不锈钢发酵罐应力腐蚀裂纹探讨[J].机电技术,2003(2):36-39.
【7】Kasiviswanathan K V,Muralidharan N G,Raghu N,et al.Corrosion related failure of austenitic stainless steel components[C]//Corrosion of austenitic stainless steels.India:Narosa Publishing House,2002.
【8】刘正东,张国福.奥氏体不锈钢炉体应力腐蚀破裂失效分析[J].当代化工,2004,33(6):357-360.
【9】宋义全,武俊伟,李晓刚,等.常压塔顶316L不锈钢换热器管束的腐蚀失效分析[J].腐蚀科学与防护技术,2004,16(5):334-336.
【10】刘志盈.抗应力腐蚀开裂的选材标准化问题探讨[J].航天标准化,2005(4):39-42.
【11】钢制压力容器(二、相关标准)[M].北京:学苑出版社,1989.
相关信息