钼板轧制工艺的优化
Optimization of Rolling Process for Molybdenum Sheet
摘 要
钼板轧制工艺过程难以控制,轧废现象严重、成品率低,导致生产成本增大,因而寻求适宜的加工工艺势在必行.旧轧制工艺存在的问题是加热温度、初火次变形率等选择不当.新工艺将加热温度控制在1 250 ℃,初火次变形率选为37.5%.结果表明:采用新工艺不仅能提高钼板的轧制质量,还能提高钼板的综合性能.
轧制工艺
成品率
Mo sheet
rolling process
rate of finished products
Abstract
Because it is difficult to control rolling process of molybdenum sheet,there is much defective material and low rate of finished products.Therefore,it is crucial to find out a feasible rolling process.The problems of the current rolling processes are analyzed.Heating temperature,strain rate for the first run are key parameters for the consequent operations.The heating temperature should be controlled at about 1 250 ℃,and the strain rate for the first run should be about 37.5%.
中图分类号 TG337
所属栏目
基金项目
收稿日期 2006/3/22
修改稿日期 2006/5/30
网络出版日期
作者单位点击查看
备注朱爱辉(1978-),男,河北邢台人,硕士研究生.
引用该论文: ZHU Ai-hui,WANG Kuai-she,Lv Xin-kuang. Optimization of Rolling Process for Molybdenum Sheet[J]. Materials for mechancial engineering, 2007, 31(2): 26～28
朱爱辉,王快社,吕新矿. 钼板轧制工艺的优化[J]. 机械工程材料, 2007, 31(2): 26～28
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】石明柱,李林,王宝芝,等.高品质宽副钼板的研制[J].中国钼业,2004,28(2):46-47.
【2】杨明杰,李麦海,魏忠梅.轧制温度对钼板组织与性能的影响[J].稀有金属与硬质合金,1999,26(2):31-32.
【3】稀有金属材料加工手册编辑组.稀有金属材料加工手册[M].北京:冶金工业出版社,1984:400-470.
【4】韩强,张相一.纯钼板及钼合金板热轧工艺探讨[J].中国钼业,2001,25(1):40-42.
【5】姜晓光,惠保卫.制备单根大重量喷涂钼丝的生产研究[J].中国钼业,2003,27(5):35-36.
【2】杨明杰,李麦海,魏忠梅.轧制温度对钼板组织与性能的影响[J].稀有金属与硬质合金,1999,26(2):31-32.
【3】稀有金属材料加工手册编辑组.稀有金属材料加工手册[M].北京:冶金工业出版社,1984:400-470.
【4】韩强,张相一.纯钼板及钼合金板热轧工艺探讨[J].中国钼业,2001,25(1):40-42.
【5】姜晓光,惠保卫.制备单根大重量喷涂钼丝的生产研究[J].中国钼业,2003,27(5):35-36.
相关信息