冷凝塔地脚螺栓断裂失效分析

冷凝塔地脚螺栓断裂失效分析

Failure Analysis on Barb Bolt of a Condensing Tower

谷志刚

杜宏建

李伟航

由向群

摘要

通过宏观、化学成分、金相、断口与能谱分析等方法,对冷凝塔地脚螺栓的断裂进行了失效分析.结果表明:螺栓在服役2 a后就发生了断裂,主要是因为螺栓加工不良和钢中存在严重的偏析与夹杂物等冶金缺陷;在交变拉应力作用下,使得螺栓在螺纹沟处发生脆性疲劳断裂.

标签地脚螺栓

断口

冶金缺陷

疲劳断裂

barb bolt

fracture surface

metallurgical defect

fatigue fracture

Abstract

The failure of the barb bolts in a condensing tower was studied by means of macrostructure,composition,metallography,fractography,EDS etc.The bolts was fractured after used for two years,resulting from bad working and serious metallurgical defects ,such as segregation and inclusion.The cracks are originated in the bottom of the screw thread due to fatigue fracture.

中图分类号 TG146.1

所属栏目

基金项目

收稿日期 2006/3/27

修改稿日期 2006/6/25

网络出版日期

作者单位点击查看

备注谷志刚(1954-),男,辽宁锦州人,教授级高级工程师,学士.

引用该论文: GU Zhi-gang,DU Hong-jian,LI Wei-hang,YOU Xiang-qun. Failure Analysis on Barb Bolt of a Condensing Tower[J]. Materials for mechancial engineering, 2007, 31(2): 59～61
谷志刚,杜宏建,李伟航,由向群. 冷凝塔地脚螺栓断裂失效分析[J]. 机械工程材料, 2007, 31(2): 59～61

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】束德林.工程材料力学性能[M].北京:机械工业出版社,2004.

【2】GB 1979-1980.结构钢低倍组织缺陷评级图[S].

【3】GB 10561-1989.钢中非金属夹杂物显微评定方法[S].

【4】范厚军.紧固件手册[M].南昌:江西科学技术出版社,2004.

相关信息

	标题	相关频次
	换热器紧固螺栓的应力腐蚀断裂分析	6
	蒸汽管线三通管的泄漏原因分析	6
	储气塔阀门紧固螺栓的断裂分析	4
	H13热作模具钢冲头的早期断裂原因	3
	进口氢气压缩机螺栓断裂原因分析	3
	新氢压缩机缸盖螺栓断裂机理及对策	3
	0Cr16Ni6热轧退火钢螺纹定位销断裂原因	2
	0Cr17Ni7Al钢制受电弓扭簧断裂原因分析	2
	10 t吊钩断裂原因分析	2
	18CrNiMo7-6A钢减速机输出轴断裂原因	2
	20CrNiMo钢销轴断裂原因	2
	3 044 t/h超超临界锅炉磨煤机拉杆断裂原因	2
	316L不锈钢泵轴断裂原因分析	2
	316L不锈钢过滤网断裂原因分析	2
	34CrNi3Mo钢制轧辊断裂原因分析	2
	35CrMo钢带泵轴断裂原因分析	2
	35CrMo钢高强螺栓断裂失效分析	2
	35CrMo螺栓断裂分析	2
	3Cr2W8V合金钢轴承套圈用热挤压芯棒断裂失效分析	2
	40CrNiMo钢主轴断裂原因分析	2
	40Cr钢机油泵轴断裂分析	2
	40Cr钢汽车转向弯臂断裂原因	2
	42CrMo钢三棱螺旋钻杆接头断裂原因分析	2
	45钢传动轴断裂原因	2
	45钢电机轴断裂分析	2
	45钢拉杆断裂失效分析	2
	48MnV非调质钢曲轴断裂的原因分析	2
	55CrSi钢气门弹簧断裂原因分析	2
	55SiCrA钢弹簧断裂原因	2
	600 MW机组次末级叶片断裂原因分析	2