Elevated Temperature Tensile Ductility of As-forged Super Duplex Stainless Steel
摘 要
用Gleeble-3800热变形模拟试验机研究了锻态00Cr25Ni7Mo4N超级双相不锈钢在900~1 300 ℃时的高温拉伸塑性和高温变形组织特征.结果表明:温度对锻态超级双相不锈钢的热塑性影响显著,在1 100~1 200 ℃具有良好的热塑性,在1 200 ℃时断面收缩率最高达到70%,温度超过1 200 ℃后,热塑性下降明显:高温固溶处理对该不锈钢的热塑性有很大的影响,固溶处理温度为1 100 ℃时,热塑性提高.
Abstract
The tensile properties at 900-1 300 ℃,as well as the deformed microstructure of the as-forged 00Cr25Ni7Mo4N super duplex stainless steel (SDSS) have been studied by thermo-mechanical simulator.The effect of temperature on the ductility of this steel is very obvious.The reduction in area (RA) of the as-forged SDSS is 70% at temperature of 1 200 ℃,and the alloy exhibited good ductility at 1 100-1 200 ℃.When the temperature is beyond 1 200 ℃,however,the hot ductility dropped remarkably.Moreover,high temperature solid solution treatment significantly influence the hot ductility of the as-forged SDSS.The hot ductility increase when the solid solution treatment temperature was 1 100℃.
中图分类号 TG146.1
所属栏目
基金项目
收稿日期 2006/7/4
修改稿日期 2006/9/20
网络出版日期
作者单位点击查看
备注童骏(1981-),男,浙江临安人,硕士研究生.
引用该论文: TONG Jun,FU Wan-tang,ZHOU Can-dong,LIN Gang,SONG Guo-bin,SONG Hong-wei. Elevated Temperature Tensile Ductility of As-forged Super Duplex Stainless Steel[J]. Materials for mechancial engineering, 2007, 31(6): 50~52
童骏,傅万堂,周灿栋,林刚,宋国斌,宋洪伟. 锻态超级双相不锈钢的高温拉伸塑性[J]. 机械工程材料, 2007, 31(6): 50~52
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Park Y H,Lee Z H.The effect of nitrogen and heat treatment on the microstructure and tensile properties of 25Cr-7Ni-1.5N-3W-xN duplex stainless steel castings[J].Mater Sci Eng,2001,A297(1):78-84.
【2】Iacoviello F,Casari F,Gialanella S.Effect of “475 ℃ embrittlement” on duplex stainless steels localized corrosion resistance[J].Corros Sci,2005,47(4):909-922.
【3】Maki T,Furuhara T,Tsuzaki K.Microstructure development by thermomechanical processing in duplex stainless steel[J].ISIJ Int,2001,41(6):571-579.
【4】Miranda M A R,Sasaki J M,Tavares S S M,et al.The use of X-ray diffraction,microscopy,and magnetic measurements for analysing microstructural features of a duplex stainless steel[J].Mater Charact,2005,54(4):387-393.
【5】Cabrera J M,Mateo A,Llanes L,et al.Hot deformation of dupleu stainless steels[J].J Mater Process Technol,2003,143/144(20):321-325.
【6】吴玖.双相不锈钢[M].北京:冶金工业出版社,1999:2-4.
【7】Duprez L,De Cooman B C,Akdut N.Flow stress and ductility of duplex stainless steel during high-temperature torsion deformation[J].Metall Mater Trans,2002,33A(7):1931-1938.
【8】《彩色金相技术》编写组.彩色金相技术(原理及方法)[M].北京:国防工业出版社,1987:119.
【9】Martins M,Casteletti L C.Heat treatment temperature influence on ASTM A890 GR 6A super duplex stainless steel microstructure[J].Mater Charact,2005,55(3):225-233.
【2】Iacoviello F,Casari F,Gialanella S.Effect of “475 ℃ embrittlement” on duplex stainless steels localized corrosion resistance[J].Corros Sci,2005,47(4):909-922.
【3】Maki T,Furuhara T,Tsuzaki K.Microstructure development by thermomechanical processing in duplex stainless steel[J].ISIJ Int,2001,41(6):571-579.
【4】Miranda M A R,Sasaki J M,Tavares S S M,et al.The use of X-ray diffraction,microscopy,and magnetic measurements for analysing microstructural features of a duplex stainless steel[J].Mater Charact,2005,54(4):387-393.
【5】Cabrera J M,Mateo A,Llanes L,et al.Hot deformation of dupleu stainless steels[J].J Mater Process Technol,2003,143/144(20):321-325.
【6】吴玖.双相不锈钢[M].北京:冶金工业出版社,1999:2-4.
【7】Duprez L,De Cooman B C,Akdut N.Flow stress and ductility of duplex stainless steel during high-temperature torsion deformation[J].Metall Mater Trans,2002,33A(7):1931-1938.
【8】《彩色金相技术》编写组.彩色金相技术(原理及方法)[M].北京:国防工业出版社,1987:119.
【9】Martins M,Casteletti L C.Heat treatment temperature influence on ASTM A890 GR 6A super duplex stainless steel microstructure[J].Mater Charact,2005,55(3):225-233.
相关信息