Continuous Cooling Transformation Curves of High Vanadium High Speed Steel
摘 要
利用Gleeble1500D型热模拟试验机测定了新型高钒高速钢在1 000 ℃奥氏体化后以不同冷却速率冷却时的相变膨胀曲线,并用Origin软件绘制了该钢的连续冷却转变 (CCT) 曲线.结果表明:高钒高速钢在连续冷却过程中存在珠光体、贝氏体和马氏体转变;当冷却速率在0.25 ℃/s时,能获得珠光体、贝氏体、马氏体与奥氏体的混合组织;马氏体开始转变的临界冷却速率约为0.5 ℃/s ,其开始转变点Ms低于200 ℃,且随着冷却速率的增大而降低.
Abstract
The swelling capacity in high vanadium high speed steel after austenitizing at 1 000 ℃ and at different cooling rates was tested using a Gleeble 1500D thermal simulation testing machine.The expansion curves of phase transformation and the continuous cooling transformation (CCT) curves have been drawn by Origin software.The results show that the transformation of perlite,bainite and martensite occurre in the continuous cooling process.Perlite,bainite,martensite and residual austenite could be obtained at the cooling rate of 0.25 ℃/s.The critical cooling rate of the steel is 0.5 ℃/s.The martensite start transformation Ms is lower than 200 ℃ and decreases with the increase of cooling rate.
中图分类号 TG146.1
所属栏目
基金项目 河南省重大科技攻关项目(0322020300)
收稿日期 2006/10/13
修改稿日期 2007/1/15
网络出版日期
作者单位点击查看
备注季英萍(1981-),女,山东临沂人,硕士研究生.
引用该论文: JI Ying-ping,LI Yan,WEI Shi-zhong,LONG Rui,XU Liu-jie. Continuous Cooling Transformation Curves of High Vanadium High Speed Steel[J]. Materials for mechancial engineering, 2007, 31(7): 63~65
季英萍,李炎,魏世忠,龙锐,徐流杰. 高钒高速钢连续冷却转变曲线的测定与分析[J]. 机械工程材料, 2007, 31(7): 63~65
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Sano Y,Hattori T,Haga M.Characteristics of high carbon high speed steel rolls for hot Strip mill[J].ISIJ International,1992,32(11):1194-1201.
【2】Goto T,Matsuda Y,Sakamoto K,et al.Basic characteristics and microstructure of high-carbon high speed steel rolls for hot rolling mill[J].ISIJ International,1992,32(11):1184-1189.
【3】HWANG Keun Chul,LEE Sunghak,LEE Hui Choon.Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls[J].Materials Science and Engineering A,1998,254:282-295.
【4】刘海峰,刘耀辉,于思荣.高碳高钒系高速钢的耐磨性研究[J].摩擦学学报,2000,20(6):401-406.
【5】王金国,周宏,苏源德,等.高碳高钒高速钢的高温硬度及热处理的研究[J].金属热处理,2000(3):22-24.
【6】魏世忠,龙锐.高钒高耐磨合金锤头的研制及使用[J].水泥,2001(8):31-33.
【7】林慧国,傅代直.钢的奥氏体转变曲线原理测试与应用[M].北京:机械工业出版社,1988.
【8】李壮,张平礼,王佳夫,等.硅-锰系TRIP钢热处理工艺的研究[J].机械工程材料,2004,28(12):42-45.
【9】马艳丽,康永林,王建泽.高强耐候钢相变组织变化规律研究[J].机械工程材料,2006,30(1):12-15.
【2】Goto T,Matsuda Y,Sakamoto K,et al.Basic characteristics and microstructure of high-carbon high speed steel rolls for hot rolling mill[J].ISIJ International,1992,32(11):1184-1189.
【3】HWANG Keun Chul,LEE Sunghak,LEE Hui Choon.Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls[J].Materials Science and Engineering A,1998,254:282-295.
【4】刘海峰,刘耀辉,于思荣.高碳高钒系高速钢的耐磨性研究[J].摩擦学学报,2000,20(6):401-406.
【5】王金国,周宏,苏源德,等.高碳高钒高速钢的高温硬度及热处理的研究[J].金属热处理,2000(3):22-24.
【6】魏世忠,龙锐.高钒高耐磨合金锤头的研制及使用[J].水泥,2001(8):31-33.
【7】林慧国,傅代直.钢的奥氏体转变曲线原理测试与应用[M].北京:机械工业出版社,1988.
【8】李壮,张平礼,王佳夫,等.硅-锰系TRIP钢热处理工艺的研究[J].机械工程材料,2004,28(12):42-45.
【9】马艳丽,康永林,王建泽.高强耐候钢相变组织变化规律研究[J].机械工程材料,2006,30(1):12-15.
相关信息