以活性炭为模板制备纳米ZrO2粉体
Preparation of ZrO2 Nanoparticles Using Active Carbon as Template
摘 要
以活性炭为模板,尿素为沉淀剂,用沉积沉淀煅烧法制备了ZrO2纳米粉体,利用热重法(TG)、X射线衍射仪(XRD)、比表面积(BET)和扫描电子显微镜(SEM)等对粉体进行了表征.结果表明:加入活性炭后,前驱体在400 ℃以下质量损失较小,在400~600 ℃阶段损失较大,在600 ℃以上质量基本没有变化;活性炭的加入对ZrO2的粉体粒径影响不大,但ZrO2的比表面积有明显增加;随着尿素用量的增加,粉体粒径减小,同时四方相的比例增加;当硝酸锆与尿素摩尔比为1∶8,活性炭加入量为2.500 g时,可制得粒径为12.5 nm、比表面积为43.931 m2·g-1、晶型为纯四方相的ZrO2粉体.
ZrO2
活性炭
模板
deposition-precipitation method
ZrO2
active carbon
template
Abstract
ZrO2 nanoparticles were prepared by deposition-precipitation method.The presence of active carbon could act as an interesting template.TG,XRD,BET and SEM were used to characterize the products.With active carbon,the precursor lose weight slowly before 400 ℃,fast during 400-600 ℃ and had little variation abovc 600 ℃.The addition of active carbon has no influence on the crystallite size of ZrO2,but the specific surface area became higher.The higher the CO(NH2)2 content,the lower the crystallite size and the more the tetragonal proportion.Highly pure tetragonal ZrO2 nanoparticles with the crystallite size of about 12.5 nm and the surface area of 43.931 m2·g-1 could be obtained with 1∶8 Zr(NO3)4/CO(NH2)2 mole ratio and 2.500 g active carbon.
中图分类号 TB383
所属栏目
基金项目
收稿日期 2006/9/9
修改稿日期 2007/1/23
网络出版日期
作者单位点击查看
备注王科(1982-),男,江苏常州人,硕士研究生.
引用该论文: WANG Ke,CHEN Hong-ling. Preparation of ZrO2 Nanoparticles Using Active Carbon as Template[J]. Materials for mechancial engineering, 2007, 31(8): 70～72
王科,陈洪龄. 以活性炭为模板制备纳米ZrO2粉体[J]. 机械工程材料, 2007, 31(8): 70～72
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Kresge C T,Leonowicz M E,Roth W J,et al.Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism[J].Nature,1992,359:710-712.
【2】Xinyi Zhang,Baodian Yao,Lixia Zhao,et al.Electrochemical fabrication of single-crystalline anatase TiO2 nanowire arrays[J].Journal of The Electrochemical Society,2001,148(7):398-400.
【3】杨儒,郭亮.纳米管状结构立方萤石型CeO2的合成[J].无机化学学报,2004,20(2):152-158.
【4】李威,刘丽芬,杨凤林,等.以ACF为模板制备掺氮TiO2及其光催化脱氨氮研究[J].感光科学与光化学,2005,23(5):374-381.
【5】高雪琴,张景林,王作山.纳米镍粉及其连续制备方法[J].安徽化工,2006,141(3):34-36.
【6】Qun Xu,Kunlun Ding,Liumin He,et al.A new mechanism about the process of preparing nanoporous silica with activated carbon mold[J].Materials Science and Engineering B,2005,121(3):266-271.
【7】Colón G,Hidalgo M C,Navio J A.A novel preparation of high surface area TiO2 nanoparticles from alkoxide precursor and using active carbon as additive[J].Catalysis Today,2002,76(2):91-101.
【8】Garvie R C,Alper M.High temperature oxides part Ⅱ[M].New York:Academic Press,1970:117-118.
【9】王焕英,宋秀芹,陈汝芬.以尿素为沉淀剂制备纳米氧化锆的研究[J].河北师范大学学报(自然科学版),2004,28(2):162-165.
【10】Rov R.Ceramics by the solution-sol-gel route[J].Science,1987,238(12):1664-669.
【2】Xinyi Zhang,Baodian Yao,Lixia Zhao,et al.Electrochemical fabrication of single-crystalline anatase TiO2 nanowire arrays[J].Journal of The Electrochemical Society,2001,148(7):398-400.
【3】杨儒,郭亮.纳米管状结构立方萤石型CeO2的合成[J].无机化学学报,2004,20(2):152-158.
【4】李威,刘丽芬,杨凤林,等.以ACF为模板制备掺氮TiO2及其光催化脱氨氮研究[J].感光科学与光化学,2005,23(5):374-381.
【5】高雪琴,张景林,王作山.纳米镍粉及其连续制备方法[J].安徽化工,2006,141(3):34-36.
【6】Qun Xu,Kunlun Ding,Liumin He,et al.A new mechanism about the process of preparing nanoporous silica with activated carbon mold[J].Materials Science and Engineering B,2005,121(3):266-271.
【7】Colón G,Hidalgo M C,Navio J A.A novel preparation of high surface area TiO2 nanoparticles from alkoxide precursor and using active carbon as additive[J].Catalysis Today,2002,76(2):91-101.
【8】Garvie R C,Alper M.High temperature oxides part Ⅱ[M].New York:Academic Press,1970:117-118.
【9】王焕英,宋秀芹,陈汝芬.以尿素为沉淀剂制备纳米氧化锆的研究[J].河北师范大学学报(自然科学版),2004,28(2):162-165.
【10】Rov R.Ceramics by the solution-sol-gel route[J].Science,1987,238(12):1664-669.
相关信息