锯片钢75Cr1连铸板坯裂纹成因初探
Analyses for Cracks in Cast Slab of Saw Steel 75Cr1
摘 要
通过光学显微镜、扫描电镜和电子探针,分析了锯片钢75Cr1高碳钢生产过程中连铸板坯产生裂纹的原因.结果表明：板坯裂纹源产生于距连铸板坯表面30~50 mm之间,裂纹产生和扩展与碳偏析、网状铁素体沿晶界析出及铸态高碳珠光体止裂能力差等因素有关.
连铸板坯
裂纹
saw steel
continuous cast slab
crack
Abstract
The mechanism for cracking of slab made of 75Cr1 saw steel was investigated by means of optical metallography,scanning electron microscopy and electron probe analysis.The cracks are initiated at a depth of 30-50 mm from the surface of the slab,being associated with carbon segregation,ferrite precipitation at grain boundaries and low crack arresting capability of high carbon as-cast pearlite.
中图分类号 TG115.21
所属栏目
基金项目
收稿日期 2006/9/2
修改稿日期 2007/2/28
网络出版日期
作者单位点击查看
备注欧鹏(1973-),男,上海人,助理工程师,硕士.
引用该论文: OU Peng,JIANG Lai-zhu,YANG Feng,ZHANG Han-qian. Analyses for Cracks in Cast Slab of Saw Steel 75Cr1[J]. Materials for mechancial engineering, 2007, 31(8): 76～78
欧鹏,江来珠,杨峰,张汉谦. 锯片钢75Cr1连铸板坯裂纹成因初探[J]. 机械工程材料, 2007, 31(8): 76～78
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】熊临敞.高碳钢连铸工艺优化[J].冶金信息导刊,2004(5):22-25.
【2】史宸兴.连铸钢坯质量[M].北京:冶金工业出版社,1980.
【3】薛正良.高碳钢连铸方坯中心偏析[J].炼钢,2000(1):56-59.
【4】武建民.方坯连铸机浇铸高碳钢[J].南方金属,2003(2):4-8.
【5】廖永松.轻压下技术在高碳钢方坯连铸中的应用[J].炼钢,2002(5):35-39.
【2】史宸兴.连铸钢坯质量[M].北京:冶金工业出版社,1980.
【3】薛正良.高碳钢连铸方坯中心偏析[J].炼钢,2000(1):56-59.
【4】武建民.方坯连铸机浇铸高碳钢[J].南方金属,2003(2):4-8.
【5】廖永松.轻压下技术在高碳钢方坯连铸中的应用[J].炼钢,2002(5):35-39.
相关信息