K18合金增压器涡轮叶片断裂故障分析
Failure Analysis of Blade Fracture in Supercharger Turbo Made of K18 Alloy
摘 要
采用体视显微镜、扫描电镜等分析手段对K18合金增压器涡轮铸造叶片的断裂形貌与断裂机制等进行了分析.结果表明:涡轮中有一断裂破坏面最为明显的叶片是先断裂的,然后造成其它叶片不同程度的碰伤;从叶片断口特征判定,先断裂叶片在高转速、高燃气温度下首先发生疲劳断裂,其裂纹源起始于距叶根约1 cm处次表皮下面的一处铸造缺陷——冷隔.
K18合金
疲劳断裂
铸造缺陷
supercharger turbo
K18 superalloy
fatigue fracture
casting defect
Abstract
By means of stereomicroscopy and scanning electronic microscopy(SEM),the fracture mode and mechanism of the broken K18 superalloy cast blade in a supercharger turbo were investigated.A blade with a heavy fracture appearance has been confirmed to be the source of the accident,and some other blades displaye damage with various degrees.The fracture mechanism of this blade is due to fatigue fracture under conditions of high rotational speed and high temperature,and the crack source of this blade is a casting defect of cold shut located beneath the subsurface of this blade for 1 cm.
中图分类号 TG146.1
所属栏目
基金项目
收稿日期 2006/11/2
修改稿日期 2007/3/1
网络出版日期
作者单位点击查看
备注蒙肇斌(1968-),男,广西灵山人,副教授,博士.
引用该论文: MENG Zhao-bin,ZEN Bao-lin,ZHANG Ji,WANG Yan-qing. Failure Analysis of Blade Fracture in Supercharger Turbo Made of K18 Alloy[J]. Materials for mechancial engineering, 2007, 31(9): 73～75
蒙肇斌,甄宝林,张继,王延庆. K18合金增压器涡轮叶片断裂故障分析[J]. 机械工程材料, 2007, 31(9): 73～75
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国航空材料手册编辑委员会.中国航空材料手册[M].北京:中国标准出版社,2002.
【2】黄乾尧,李汉康.高温合金[M].北京:冶金工业出版社,2000.
【3】高温合金金相图谱编辑委员会.高温合金金相图谱[M].北京:冶金工业出版社,1979.
【4】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2004.
【5】比利P R.铸造工艺学[M].北京:机械工业出版社.1986.
【6】Henry G,Hcrstmann D.宏观断口学及显微断口学[M].北京:机械工业出版社.1990.
【2】黄乾尧,李汉康.高温合金[M].北京:冶金工业出版社,2000.
【3】高温合金金相图谱编辑委员会.高温合金金相图谱[M].北京:冶金工业出版社,1979.
【4】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2004.
【5】比利P R.铸造工艺学[M].北京:机械工业出版社.1986.
【6】Henry G,Hcrstmann D.宏观断口学及显微断口学[M].北京:机械工业出版社.1990.
相关信息