钴-铬-钨合金焊丝的制备及性能
Preparation of Co-Cr-W Welding Electrode and Research on Its Performance
摘 要
采用真空吸铸方法制备出了性能优良的钴-铬-钨合金焊丝,并对其进行了堆焊性能测试.结果表明：焊丝的堆焊性能良好,焊层与基材形成了良好的冶金结合,堆焊层的平均硬度达到了40.2 HRC,并且堆焊三层后硬度达到41 HRC;各层的化学成分较为均匀.
合金焊丝
堆焊
Co-Cr-W alloy
welding electrodes
surfacing welding
Abstract
A new Co-Cr-W welding electrode was prepared by technical innovation suction casting device,and the overlaying property of this electrode was tested.The results indicate that the binding between alloy layer and matrix is excellent,on welding layer substrate,which is metallurgical binding.The mean Rockwell hardness of welding layer is 40.2 and the hardness reaches maximum value,after overlaying three layers of Co-Cr-W alloy.Chemical constituents of welding layer is homogenous.
中图分类号 TG146.1
所属栏目
基金项目
收稿日期 2007/2/14
修改稿日期 2007/9/14
网络出版日期
作者单位点击查看
备注贾志华(1980-),男,陕西西安人,助理工程师,硕士.
引用该论文: JIA Zhi-hua,MA Guang,ZHENG Jing,WANG Yi,LI Yin-e. Preparation of Co-Cr-W Welding Electrode and Research on Its Performance[J]. Materials for mechancial engineering, 2007, 31(11): 24～25
贾志华,马光,郑晶,王轶,李银娥. 钴-铬-钨合金焊丝的制备及性能[J]. 机械工程材料, 2007, 31(11): 24～25
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周振丰.金属熔焊原理及工艺[M].北京:机械工业出版社,1981:284.
【2】刘玉珍,桂业炜.钴铬钨合金的应用[J].机械工程材料,1992(5):1-4.
【3】常安国,洪海生.CLA法真空吸铸工艺[J].中国铸造装备与技术,1996(1):10-14.
【4】克先诺方托夫.真空吸铸法[M].陈立波,译.北京:国防工业出版社,1958.
【2】刘玉珍,桂业炜.钴铬钨合金的应用[J].机械工程材料,1992(5):1-4.
【3】常安国,洪海生.CLA法真空吸铸工艺[J].中国铸造装备与技术,1996(1):10-14.
【4】克先诺方托夫.真空吸铸法[M].陈立波,译.北京:国防工业出版社,1958.
相关信息