异步轧制速比对低硅无取向硅钢冷轧织构的影响
Effect of Speed Ratio in Cross Shear Rolling on Texture of Non-orientated Low Silicon Steel
摘 要
选取低硅无取向硅钢常化态板材,分别在不同速比下进行异步轧制,考察了速比对低硅无取向硅钢冷轧织构的影响.结果表明：异步冷轧织构主要是由α织构、γ织构及反高斯织构等织构组分组成,快辊侧和慢辊侧的主要织构组分没有什么差别;但进一步的定量分析计算可以看出,慢辊侧α织构的取向密度明显高于快辊侧,γ织构的取向密度差别不大;在试验所选的各速比中,低速比下的织构强度高于高速比下的织构强度.
速比
硅钢
织构
cross shear rolling
speed ratio
silicon steel
texture
Abstract
In order to further improve the efficiency of electronics,the ferromagnetic loss needs to be lowered down.The effect of speed ratio on the texture of non-oriented cold rolled low silicon steel sheet was investigated after cross shear rolling at different speed ratios.The experimental results show that the main textures are made of α-texture,γ-texture and anti-Goss texture.The main texture components have no variation along the fast or slow speed roller side.However,the further quantitative calculation analysis results show that the orientation density of the α-texture along the slow speed roller side is more than that along the fast speed roller side and the orientation density of the γ-texture did not vary too much.The different speed ratios,the texture density at the low speed ratio is higher than that at the high speed ratio.
中图分类号 TG142.1 TG142.77
所属栏目
基金项目 国家高技术研究发展计划资助项目(2003AA331080)
收稿日期 2006/11/21
修改稿日期 2007/3/30
网络出版日期
作者单位点击查看
备注张正贵(1964-),男,山东临朐人,副教授,博士研究生.
引用该论文: ZHANG Zheng-gui,YAO Xu-sheng,ZHU Xiao-bo,ZUO Liang,WANG Fu. Effect of Speed Ratio in Cross Shear Rolling on Texture of Non-orientated Low Silicon Steel[J]. Materials for mechancial engineering, 2007, 31(12): 8～10
张正贵,姚旭升,祝晓波,左良,王福. 异步轧制速比对低硅无取向硅钢冷轧织构的影响[J]. 机械工程材料, 2007, 31(12): 8～10
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】何忠治.电工钢[M].北京:冶金工业出版社,1996:276.
【2】毛卫民,余永宁.金属材料各向异性的开发研究[J].金属热处理学报,1997,18(3):95-100.
【3】李军,杜炳坤.无取向硅钢薄带的研究[J].金属功能材料,1997(2):79-81.
【4】张文康,毛卫民,王一德,等.热轧工艺对无取向硅钢组织结构和磁性能的影响[J].钢铁,2006,41(4):77-81.
【5】张新仁,谢晓心.高磁感无取向硅钢[J].钢铁研究,2000(4):57-61.
【6】孙述利,郭东城,刘江,等.形变对无取向硅钢50W470组织和力学性能的影响[J].特殊钢,2005,26(5):14-15.
【7】高秀华,叶何舟,邱春林,等.无取向硅钢薄带的开发[J].钢铁,2007,27(2):60-63.
【8】刘刚,王福,齐克敏,等.异步轧制取向硅钢中织构沿板厚方向的分布与发展[J].金属学报,1997,33(4):364-369.
【9】刘刚,齐克敏,贺会军,等.异步轧制取向硅钢的织构形成与转变机理[J].钢铁研究学报,1999,11(5):30-33.
【10】沙玉辉,刘 恩,徐家桢,等.磁场作用下取向硅钢薄带的再结晶织构[J].东北大学学报,2004,25(7):665-667.
【11】高秀华,齐克敏,叶何舟,等.异步轧制对硅钢极薄带三次再结晶的影响[J].材料科学与工艺,2005,13(4):384-386.
【12】Liang Z,Xu J,Wang F.Determination of ODF of polycrystalline materials from incomplete pole figures[C]//Proc 6th Int Conf on Textures of Materials,Vol.2.Tokyo:ISIJ,1981:1259-1265.
【13】Hotaka Homma,Naoki Yoshinaga,Masaaki Sugiyama,et al.Micro-scale orientation study on RD//〈011〉cold rolling texture and the recrystallisation in steel[J].Materia Japan,2001,40(7):650-654.
【2】毛卫民,余永宁.金属材料各向异性的开发研究[J].金属热处理学报,1997,18(3):95-100.
【3】李军,杜炳坤.无取向硅钢薄带的研究[J].金属功能材料,1997(2):79-81.
【4】张文康,毛卫民,王一德,等.热轧工艺对无取向硅钢组织结构和磁性能的影响[J].钢铁,2006,41(4):77-81.
【5】张新仁,谢晓心.高磁感无取向硅钢[J].钢铁研究,2000(4):57-61.
【6】孙述利,郭东城,刘江,等.形变对无取向硅钢50W470组织和力学性能的影响[J].特殊钢,2005,26(5):14-15.
【7】高秀华,叶何舟,邱春林,等.无取向硅钢薄带的开发[J].钢铁,2007,27(2):60-63.
【8】刘刚,王福,齐克敏,等.异步轧制取向硅钢中织构沿板厚方向的分布与发展[J].金属学报,1997,33(4):364-369.
【9】刘刚,齐克敏,贺会军,等.异步轧制取向硅钢的织构形成与转变机理[J].钢铁研究学报,1999,11(5):30-33.
【10】沙玉辉,刘 恩,徐家桢,等.磁场作用下取向硅钢薄带的再结晶织构[J].东北大学学报,2004,25(7):665-667.
【11】高秀华,齐克敏,叶何舟,等.异步轧制对硅钢极薄带三次再结晶的影响[J].材料科学与工艺,2005,13(4):384-386.
【12】Liang Z,Xu J,Wang F.Determination of ODF of polycrystalline materials from incomplete pole figures[C]//Proc 6th Int Conf on Textures of Materials,Vol.2.Tokyo:ISIJ,1981:1259-1265.
【13】Hotaka Homma,Naoki Yoshinaga,Masaaki Sugiyama,et al.Micro-scale orientation study on RD//〈011〉cold rolling texture and the recrystallisation in steel[J].Materia Japan,2001,40(7):650-654.
相关信息