Optimizing of Processing Parameters for NC CO2 Laser Welding of DOGAL 800DP Zinc Coated High Strength Steel
摘 要
采用正交方法优化试验方案,对DOGAL 800DP镀锌高强钢进行激光焊接试验,并对激光焊接试样进行了多种焊接质量的检测.结果表明:数控CO2激光焊接1.5 mm厚镀锌高强钢时,在试验条件下保证焊缝成形、强度和质量的优化工艺参数是以氮气作为保护气体,同轴气流量为3.0 m3·h-1,激光功率1 300 W,离焦量-0.4 mm,焊接速度0.80 m·min-1,侧吹气流与水平方向成40°夹角,侧吹气流量2.1 m3·h-1.
Abstract
Welding seams were tested and experiment of laser welding of DOGAL 800DP zinc coated high strength steel was performed using orthogonal test method.The optimum processing parameter for numeric control CO2 laser welding of zinc coated high strength steel with 1.5 mm thickness are as follows:adopting N2 as protective gas,coaxial gas feed rate of 3.0 m3·h-1,laser power of 1 300 W,defocusing amount of -0.4 mm,welding speed at 0.8 m·min-1,corner dimension with horizontal direction of side blown gas at 40°,gas feed rate of side blown gas at 2.1 m3·h-1.
中图分类号 TG174.44
所属栏目
基金项目 国家自然科学基金资助项目(50575070)
收稿日期 2007/4/5
修改稿日期 2007/10/10
网络出版日期
作者单位点击查看
备注申晓龙(1964-),男,湖南隆回人,副教授,硕士.
引用该论文: SHEN Xiao-long,DONG Jian-guo,PENG Yue-xiang,CHEN Gen-yu,PI Zhi-mou. Optimizing of Processing Parameters for NC CO2 Laser Welding of DOGAL 800DP Zinc Coated High Strength Steel[J]. Materials for mechancial engineering, 2008, 32(2): 40~43
申晓龙,董建国,彭跃湘,陈根余,皮智谋. DOGAL 800DP镀锌高强钢数控CO2激光焊接工艺参数的优化[J]. 机械工程材料, 2008, 32(2): 40~43
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】崔怀洋,陈铠,左铁钏,等.镀锌钢板的CO2激光焊焊接性[J].焊接学报,2004,25(4):114-120.
【2】李力钧,陈根余.折叠式准封离型CO2激光器及其在切割和焊接中的应用[J].制造技术与机床,2004(2):34-36.
【3】Zhang Xudong,Chen Wuzhu,Jiang Ping,et al.Modeling and applications of plasma charge current in laser welding[J].Journal of Applied Physics,2003,93(11):45-48.
【4】Ming f.sh.i.Advanced High Strength Steels Properties Performances and Applications[C]//China-America Automotive Materials Seminar.Detroit:MI,2003:112-114.
【5】李善术.数控机床及其应用[M].北京:机械工业出版社,2003.
【6】申晓龙.高强度镀锌钢激光焊接质量的研究[D].长沙:湖南大学,2006.
【7】Khersonsky A,Lee H.Induction heating for efficient laser application[J].Advanced Materials & Process,2000(4):20-27.
【8】Lei Hong.The study of stability model of laser welding aluminium alloys and the influence of heat input parameters to the stability[D].Beijing:Tsinghua University,2003.
【9】王成.400 MPa级钢激光焊接及其焊接性研究[D].北京:清华大学,2002.
【2】李力钧,陈根余.折叠式准封离型CO2激光器及其在切割和焊接中的应用[J].制造技术与机床,2004(2):34-36.
【3】Zhang Xudong,Chen Wuzhu,Jiang Ping,et al.Modeling and applications of plasma charge current in laser welding[J].Journal of Applied Physics,2003,93(11):45-48.
【4】Ming f.sh.i.Advanced High Strength Steels Properties Performances and Applications[C]//China-America Automotive Materials Seminar.Detroit:MI,2003:112-114.
【5】李善术.数控机床及其应用[M].北京:机械工业出版社,2003.
【6】申晓龙.高强度镀锌钢激光焊接质量的研究[D].长沙:湖南大学,2006.
【7】Khersonsky A,Lee H.Induction heating for efficient laser application[J].Advanced Materials & Process,2000(4):20-27.
【8】Lei Hong.The study of stability model of laser welding aluminium alloys and the influence of heat input parameters to the stability[D].Beijing:Tsinghua University,2003.
【9】王成.400 MPa级钢激光焊接及其焊接性研究[D].北京:清华大学,2002.
相关信息