硫酸蒸发器钽合金管断裂失效分析
Fracture Analysis of Tantalum Tube of Sulfuric Acid Evaporator
摘 要
苯胺装置的硫酸蒸发器材料为Ta-2.5W,其加热管使用6个月即发生断裂,对其断裂原因进行了分析.结果表明：该材料在现场介质中耐腐蚀性能极强,断裂原因不是应力腐蚀而是由于材料表面受到划伤,使得钽管承载载荷的有效区域减少,强度下降而造成的.
Ta-2.5W合金
电化学
应力腐蚀
evaporator
Ta-2.5W alloy
electrification
stress corrosion
Abstract
The failure reason of the Ta-2.5W pipe of sulphuric acid evaporator,which was put into use for only six months,was studied.The results show that the material has excellent anti-corrosion performance in the medium.The rupture was not caused by stress corrosion cracking,but induced by the surface scratch of material,resulting in a decrease of the efficient loading area of tantalum pipe thus reduction of strength.
中图分类号 TQ050.9
所属栏目
基金项目
收稿日期 2007/3/22
修改稿日期 2007/6/1
网络出版日期
作者单位点击查看
备注王景阳(1974-),男,甘肃兰州人,工程师,硕士.
引用该论文: WANG Jing-yang,WANG Ying-li,WANG Zhi-lin,ZHANG Huai-zhou,WANG Xiao-hua,JIANG Wan-qiang. Fracture Analysis of Tantalum Tube of Sulfuric Acid Evaporator[J]. Materials for mechancial engineering, 2008, 32(2): 61～62
王景阳,王赢利,王值林,张怀洲,王小华,姜顽强. 硫酸蒸发器钽合金管断裂失效分析[J]. 机械工程材料, 2008, 32(2): 61～62
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】廖际常.钽和Ta-2.5%W在高浓度硫酸中的腐蚀[J].稀有金属快报,1999(5):23-25.
【2】胡忠武.钽在强腐蚀环境中的应用[J].稀有金属快报,2002(2):16-17.
【3】王镐.Ta和Ta-2.5%W在硫酸处理中的使用极限[J].稀有金属快报,2000(2):26-27.
【2】胡忠武.钽在强腐蚀环境中的应用[J].稀有金属快报,2002(2):16-17.
【3】王镐.Ta和Ta-2.5%W在硫酸处理中的使用极限[J].稀有金属快报,2000(2):26-27.
相关信息