低碳高铬铸铁循环泵叶片碎裂失效分析
Failure Analysis of Cracking of a Cycle Pump Vane Made of Low Carbon High Chromium Cast Iron
摘 要
用扫描电镜、能谱分析、光学显微镜等手段对碎裂失效的低碳高铬铸铁循环泵叶片的化学成分、显微组织、断口形貌及失效机理等进行了分析及测试.结果表明：由于在一定酸性介质条件下,叶片表面发生相间选择性腐蚀,其抗冲击能力大幅下降,同时该材料的韧性较低,导致叶片早期碎裂.
高铬铸铁
腐蚀磨损
失效分析
vane
high chromium cast iron
corrosion wear
failure analysis
Abstract
The chemical composition,microstructure,fracture morphology and failure mechanism of cracking of a cycle pump vane made of low carbon high chromium cast iron were analyzed by means of SEM,EDS and optical microscopy.The results show that under the stated aciditic condition,selective corrosion between phases happened at the vane surface,and the impact-resistance dropped.The relatively low toughness of this material also resulted in anearly cracking of the vane.
中图分类号 TG143.9
所属栏目
基金项目
收稿日期 2007/4/9
修改稿日期 2007/7/2
网络出版日期
作者单位点击查看
备注哈胜男(1982-)女,江苏镇江人,硕士研究生.
引用该论文: HA Sheng-nan,REN Song-zan,XIE Chun-sheng,CHEN De-hua. Failure Analysis of Cracking of a Cycle Pump Vane Made of Low Carbon High Chromium Cast Iron[J]. Materials for mechancial engineering, 2008, 32(2): 67～70
哈胜男,任颂赞,谢春生,陈德华. 低碳高铬铸铁循环泵叶片碎裂失效分析[J]. 机械工程材料, 2008, 32(2): 67～70
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王乃华,鲁天毅.石灰石/石膏湿法烟气脱硫金属浆液循环泵国产化研究及实践[J].电力环境保护,2005,21(2):10-12.
【2】周至祥.湿式石灰石-石膏法排烟脱硫装置的问题和对策[J].四川电力技术,2001,24(1):19-25.
【3】陈璟琚,许光奎,黄兴建,等.合金高铬铸铁及其应用[M].冶金工艺出版社,1999:11-14.
【4】饶启昌,高峰,高义民.高铬铸铁腐蚀磨损特性的研究[J].铸造,1992,10:17-20.
【5】李卫,涂小慧.高铬铸铁铝矿浆泵泵壳腐蚀磨损失效分析[J].机械工程材料,2000,24(2):42-44.
【6】姜晓霞,李诗卓,李曙.金属的腐蚀磨损[M].化学工业出版社,2003:455-461,377-390.
【7】路迪民,王大业.抗磨蚀泵用过流件材质与失效分析[J].西安建筑科技大学学报,1998,30(2):15-18.
【2】周至祥.湿式石灰石-石膏法排烟脱硫装置的问题和对策[J].四川电力技术,2001,24(1):19-25.
【3】陈璟琚,许光奎,黄兴建,等.合金高铬铸铁及其应用[M].冶金工艺出版社,1999:11-14.
【4】饶启昌,高峰,高义民.高铬铸铁腐蚀磨损特性的研究[J].铸造,1992,10:17-20.
【5】李卫,涂小慧.高铬铸铁铝矿浆泵泵壳腐蚀磨损失效分析[J].机械工程材料,2000,24(2):42-44.
【6】姜晓霞,李诗卓,李曙.金属的腐蚀磨损[M].化学工业出版社,2003:455-461,377-390.
【7】路迪民,王大业.抗磨蚀泵用过流件材质与失效分析[J].西安建筑科技大学学报,1998,30(2):15-18.
相关信息