中密度钨-镍-铁粉末注射成形喂料的流变性能与流动本构模型
Rheological Property and Fluid Constitutive Relationship of Medium-density W-Ni-Fe Feedstock in Metal Injection Molding Process
摘 要
研究了中密度系列钨-镍-铁(烧结后密度分别为10,14,17 g·cm-3)粉末注射成形喂料的流变行为,分析了在相同粘结剂和粉末装载量的条件下,剪切速率、温度以及钨镍成分配比对喂料流变性能的影响.结果表明:钨-镍-铁喂料属于非牛顿型流体,遵从假塑性熔体的流动规律,具有较高的熔体粘度;其表观粘度随剪切速率的增大、温度的升高而减小;非牛顿指数随温度的升高而增大;钨在合金中所占比重越大,喂料对剪切速率的变化及温度的变化越敏感;利用非线性回归技术拟合流变参数,得到了喂料的流动本构模型.
流变性能
流动本构模型
金属注射成形
tungsten-nickel alloy
rheology property
fluid constitutive relationship
metal injection molding
Abstract
Rheology properties of three kinds of W-Ni-Fe feedstock with different densities (10,14,17 g·cm-3 respectively after sintered) were studied to determine the effect of shear rate,temperature and tungsten-nickel ratio.Results suggest that W-Ni-Fe feedstock is a kind of pseudo-plastic fluid.The apparent viscosity of the W-Ni-Fe feedstock declined as shear rate increases or temperature rised.Non-Newtonian exponent increased as temperature rised.The tungsten-nickel feedstock became more sensitive to shear rate and temperature when the ratio of tungsten increased.In addition,fluid constitutive relationship of the feedstock was derived through the non-linear fit technology.
中图分类号 TF121
所属栏目
基金项目 2005年度广东省高校科技成果转化项目(粤财教[2006]112号)
收稿日期 2007/5/25
修改稿日期 2007/8/27
网络出版日期
作者单位点击查看
备注郑振兴(1975-),男,福建福州人,博士研究生.
引用该论文: ZHENG Zhen-xing,WANG Shi-yong,XIA Wei,ZHOU Zhao-yao. Rheological Property and Fluid Constitutive Relationship of Medium-density W-Ni-Fe Feedstock in Metal Injection Molding Process[J]. Materials for mechancial engineering, 2008, 32(4): 24～28
郑振兴,王世勇,夏伟,周照耀. 中密度钨-镍-铁粉末注射成形喂料的流变性能与流动本构模型[J]. 机械工程材料, 2008, 32(4): 24～28
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李益民,曲选辉,黄伯云,等.金属注射成形喂料的流动行为及粘度参数的测定[J].稀有金属材料与工程,1997,26(1):41-43.
【2】Cao M Y,Rhee B O,Chung C I.Advance in powder metallurgy[J].Metal Powder Industries Federation,1991,2:59-63.
【3】Chee K K,Rudin A.Falling coaxial cylinder viscometer with wide shear rate range[J].Rheologica Acta,1977,16(6):1435-1528.
【4】李松林,黄伯云,曲选辉,等.金属粉末注射成形粘结剂选择的基础[J].材料导报,1999,13(2):8-9.
【5】Randall M,German,Karl F Hens.Key issues in powder injection molding[J].Ceramic Bulletin,1991,20(8):1294-1297.
【6】陈惠钊.粘度测量[M].北京:中国计量出版社,2002:142-150.
【7】李笃信,曲选辉,黄伯云,等.新型PEG基粘结剂的注射料性能研究[J].粉末冶金技术,2001,19(3):136-139.
【8】祝宝军.硬质合金注射成形工艺研究[D].长沙:中南大学,2002.
【9】邹欣,吴运新,盖国胜,等.球化处理对氢化脱氢钛粉特性及其注射成形喂料流变性能的影响[J].粉末冶金工业,2006,16(5):1-4.
【10】蒋雪璋,秦志忠.PET/PP合金流变性能的研究[J].合成技术及应用,2006,21(1):4-7.
【11】李益民,曲选辉,黄伯云,等.金属注射成形粘结剂和喂料流变性能的研究[J].粉末冶金材料科学与工程,1996,1(2):23-27.
【12】罗铁钢,曲选辉,秦明礼.注射成形合金蜡基粘结剂的优化[J].矿业研究与开发,2005,25(1):37-40.
【13】Kennedy P.Flow Analysis of Injection Molds[M].New York:Hanser Publishers,1995.
【2】Cao M Y,Rhee B O,Chung C I.Advance in powder metallurgy[J].Metal Powder Industries Federation,1991,2:59-63.
【3】Chee K K,Rudin A.Falling coaxial cylinder viscometer with wide shear rate range[J].Rheologica Acta,1977,16(6):1435-1528.
【4】李松林,黄伯云,曲选辉,等.金属粉末注射成形粘结剂选择的基础[J].材料导报,1999,13(2):8-9.
【5】Randall M,German,Karl F Hens.Key issues in powder injection molding[J].Ceramic Bulletin,1991,20(8):1294-1297.
【6】陈惠钊.粘度测量[M].北京:中国计量出版社,2002:142-150.
【7】李笃信,曲选辉,黄伯云,等.新型PEG基粘结剂的注射料性能研究[J].粉末冶金技术,2001,19(3):136-139.
【8】祝宝军.硬质合金注射成形工艺研究[D].长沙:中南大学,2002.
【9】邹欣,吴运新,盖国胜,等.球化处理对氢化脱氢钛粉特性及其注射成形喂料流变性能的影响[J].粉末冶金工业,2006,16(5):1-4.
【10】蒋雪璋,秦志忠.PET/PP合金流变性能的研究[J].合成技术及应用,2006,21(1):4-7.
【11】李益民,曲选辉,黄伯云,等.金属注射成形粘结剂和喂料流变性能的研究[J].粉末冶金材料科学与工程,1996,1(2):23-27.
【12】罗铁钢,曲选辉,秦明礼.注射成形合金蜡基粘结剂的优化[J].矿业研究与开发,2005,25(1):37-40.
【13】Kennedy P.Flow Analysis of Injection Molds[M].New York:Hanser Publishers,1995.
相关信息