新型镍基高温合金长期时效后的组织稳定性及高温性能
Microstructure Stability and High Temperature Properties of a New Nickel-base Superalloy after Long-term Aging
摘 要
利用扫描电镜研究了一种在Nimonic 263合金基础上开发的新型镍基高温合金在850 ℃长期时效后的组织稳定性及高温性能.结果表明:合金在850 ℃时效4 000 h后,主要析出相为γ′相、MC和微量的M23C6;合金时效4 000 h后未出现长条状的η相,没有发现脆化相σ相的析出,表明合金的组织是稳定的;新合金持久强度比原合金有明显提高.
长期时效
γ′相
nickel-base superalloy
long-term aging
γ′ phase
Abstract
The microstructure stability and high temperature properties of a new Ni base superalloy after long-term aging at 850 ℃ for 4 000h were investigated by SEM.The results show that the major precipitated phase of the new alloy were γ′ phase ,MC carbides and a little of M23C6 carbides after aging for 4 000 h.The η phase and σ phase were not detected in all samples.It can be concluded that the microstructure of the alloy is stable and the creep rupture strength of the new alloy had been improved greatly.
中图分类号 TG132.3
所属栏目 材料性能及其应用
基金项目
收稿日期 2007/8/26
修改稿日期 2007/10/20
网络出版日期
作者单位点击查看
备注李维银(1981-),男,宁夏海原人,硕士研究生.
引用该论文: LI Wei-yin,LIU Hong-fei,WANG Ting,ZHAO Shuang-qun. Microstructure Stability and High Temperature Properties of a New Nickel-base Superalloy after Long-term Aging[J]. Materials for mechancial engineering, 2008, 32(7): 64～67
李维银,刘红飞,王婷,赵双群. 新型镍基高温合金长期时效后的组织稳定性及高温性能[J]. 机械工程材料, 2008, 32(7): 64～67
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Tawancy H M.The Microstructure thermal stability of a nickel-base superalloy[J].J Maer Sci,1983,16:2976-2986.
【2】Lai G Y.An investigation of the thermal stability of a commercial Ni-Cr -Fe-Mo alloy(Hastelloy alloyx)[J].Mwall Trans,1978,9A:827-833.
【3】王淑荷,郭建亭,赖万慧,等.GH903高温合金650 ℃长期时效后的组织与性能[J].金属学报,1990,26(6):A432-435.
【4】Simith G D,Sizek H W.Introduction of an advanced superheater alloy for coal-fired boilers[C]//Corrosion2000.Houston:NACE Internatinal,2000:256.
【5】赵双群,谢锡善.超超临界锅炉过热器管材的高温组织稳定性及其改进研究[J].材料导报,2004,18(8):131-133.
【6】刘仲青,董建新,张麦仓,等.高温耐蚀Ni-Co-Cr高温合金的组织稳定性[J].金属学报,2002,38(5):490-494.
【7】赵双群,董建新,张麦仓,等.新一代超级超临界锅炉过热器用管材Inconel740[J].钢铁研究学报,2003,15(7):160-163.
【8】赵双群,董建新,谢锡善.Ni-Cr-Co基高温合金704 ℃和760 ℃时效组织稳定性研究[J].中国有色金属报,2003,13(3):565-569.
【9】赵双群,张麦仓,董建新,等.新型高温合金700 ℃时组织及力学性能[J].稀有金属材料与工程,2003,32(12):991-994.
【10】崔彤,王继杰,王磊,等.长期时效对一种新型镍基高温合金的组织及持久性能的影响[J].材料热处理学报,2006,27(5):56-59.
【2】Lai G Y.An investigation of the thermal stability of a commercial Ni-Cr -Fe-Mo alloy(Hastelloy alloyx)[J].Mwall Trans,1978,9A:827-833.
【3】王淑荷,郭建亭,赖万慧,等.GH903高温合金650 ℃长期时效后的组织与性能[J].金属学报,1990,26(6):A432-435.
【4】Simith G D,Sizek H W.Introduction of an advanced superheater alloy for coal-fired boilers[C]//Corrosion2000.Houston:NACE Internatinal,2000:256.
【5】赵双群,谢锡善.超超临界锅炉过热器管材的高温组织稳定性及其改进研究[J].材料导报,2004,18(8):131-133.
【6】刘仲青,董建新,张麦仓,等.高温耐蚀Ni-Co-Cr高温合金的组织稳定性[J].金属学报,2002,38(5):490-494.
【7】赵双群,董建新,张麦仓,等.新一代超级超临界锅炉过热器用管材Inconel740[J].钢铁研究学报,2003,15(7):160-163.
【8】赵双群,董建新,谢锡善.Ni-Cr-Co基高温合金704 ℃和760 ℃时效组织稳定性研究[J].中国有色金属报,2003,13(3):565-569.
【9】赵双群,张麦仓,董建新,等.新型高温合金700 ℃时组织及力学性能[J].稀有金属材料与工程,2003,32(12):991-994.
【10】崔彤,王继杰,王磊,等.长期时效对一种新型镍基高温合金的组织及持久性能的影响[J].材料热处理学报,2006,27(5):56-59.
相关信息