新型940X不锈钢的显微组织与性能
Microstructure and Property of New Stainless Steel 940X
摘 要
研究了新型940X不锈钢的淬、回火温度对其显微组织与性能的影响,并分析了940X钢淬火、回火后高硬度的机理.结果表明:940X钢最佳的淬火温度为1 030 ℃,硬度达到57.3 HRC,淬火组织为马氏体+弥散析出物;在150~500 ℃温度范围内回火,随回火温度的升高,试样的硬度先缓慢降低后再缓慢升高,在150,500 ℃回火的硬度最高,在57 HRC左右;在500~750 ℃回火后,硬度随温度升高而急剧降低;随着回火温度升高,940X钢回火组织的不同导致其硬度的变化.
热处理工艺
组织
高硬度
stainless steel 940X
heat treatment
microstructure
high hardness
Abstract
Effect of quenching and tempering temperature on microstructure and property of new stainless steel 940X were investigated and mechanism of high hardness of steel 940X after heat treatment was analyzed.The results show that the optimal quenching temperature of steel 940X was 1 030 ℃.The gained hardness was about 57.3 HRC and the microstructure was martensite and dispersed precipitates.With the increase of tempering temperature,the hardness of steel 940X decreased slowly from 150 ℃ to 300 ℃,then increased slowly from 300 ℃ to 500 ℃,and finally decreased greatly from 500 ℃ to 750 ℃.The change of tempering microstructure with temperature resulted in the change of the hardness of steel 940X.
中图分类号 TG146.1
所属栏目 新材料 新工艺
基金项目 上海市应用技术开发专项资金资助项目(05-011)
收稿日期 2007/10/9
修改稿日期 2008/3/12
网络出版日期
作者单位点击查看
备注刘晓宁(1965-),男,江西宁都人,高级工程师,学士.
引用该论文: LIU Xiao-ning,HUANG Chun-bo,SHEN Zhong-liang,XUE Chun. Microstructure and Property of New Stainless Steel 940X[J]. Materials for mechancial engineering, 2008, 32(9): 49～51
刘晓宁,黄春波,沈忠良,薛春. 新型940X不锈钢的显微组织与性能[J]. 机械工程材料, 2008, 32(9): 49～51
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】俞峰,魏果能,许达.不锈轴承材料的研究和发展[J].钢铁研究学报,2005,17(1):6-9.
【2】王玉金,叶键槢.常用不锈轴承钢的设计要点与材料[J].轴承,2004(12):37-39.
【3】魏果能,许达,俞峰,等.高纯H9Cr18不锈轴承钢的组织和性能[J].钢铁研究学报,2004,16(6):37-40.
【4】克劳斯G.钢的热处理原理[M].李崇谟,译.北京:冶金工业出版社,1987.
【2】王玉金,叶键槢.常用不锈轴承钢的设计要点与材料[J].轴承,2004(12):37-39.
【3】魏果能,许达,俞峰,等.高纯H9Cr18不锈轴承钢的组织和性能[J].钢铁研究学报,2004,16(6):37-40.
【4】克劳斯G.钢的热处理原理[M].李崇谟,译.北京:冶金工业出版社,1987.
相关信息