Recrystallization Texture of Ti-15-3 Alloy with Different Heat Treatments
摘 要
利用三维取向分布函数(ODF)并结合光学显微镜分析了经不同热处理后Ti-15-3钛合金的再结晶织构和显微组织.结果表明:对该合金固溶冷轧板在固溶温度下进行再结晶退火,当在空气炉中加热时,再结晶过程中形成γ纤维织构,并且随着晶粒的长大,γ纤维织构更加明显,此外亦形成了{114}纤维织构;在加热速率较快的盐浴炉中加热时,再结晶进程加快,γ纤维织构形成于再结晶晶粒的正常长大过程中;在空气炉中分级加热再结晶后,形成以高斯组分为主的散乱强织构.
Abstract
The recrystallization texture and microstructure of Ti-15-3 alloy with different heat treatments were investigated by means of orientation distribution function (ODF) analysis and optical microscope.The results show that in the cold-rolled sheets recrystallized in conventional annealing at the solution temperature,γ fiber textures were formed during recrystallization and then became much visible with the growth of the grain.In addition,{114} fiber textures were also generated.In the salt-bath annealing,the process of recrystallization was accelerated,and γ fiber textures developed during generally growing process of the recrystallized grains.The intensive and random textures,mainly Goss component,were formed after stage annealing.
中图分类号 TG113.12
所属栏目 试验研究
基金项目
收稿日期 2007/10/25
修改稿日期 2008/3/8
网络出版日期
作者单位点击查看
备注王环(1982-),男,四川内江人,硕士研究生.
引用该论文: WANG Huan,WU Bao-lin,DU Xing-hao,XU Qian-gang. Recrystallization Texture of Ti-15-3 Alloy with Different Heat Treatments[J]. Materials for mechancial engineering, 2008, 32(11): 20~24
王环,武保林,杜兴蒿,徐前刚. 不同条件热处理后Ti-15-3钛合金的再结晶织构[J]. 机械工程材料, 2008, 32(11): 20~24
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王庆如,张庆玲.Ti-15-3钛合金的应用研究[J].材料工程,1996(12):16-19.
【2】ZHANG De-fen,HU Zhuo-chao,ZUO Liang,et al.Evolution of textures during rolling and annealing of 3004 aluminium alloy[J].Journal of Nort Heastern University,2002,23(8):786-789.
【3】武保林,刘明玲,左良,等.Ti-15V-3Cr-3Sn-3Al板材织构与组织分析[J].材料工程,1997(增刊):41-43.
【4】沈桂琴,张庆玲,刘新华,等.Ti-15V-3Cr-3Sn-3Al合金板材的再结晶与织构特征[J].航空工艺技术,1996(6):18-20.
【5】梁志德,徐家桢,王福.织构材料的三维取向分析术——ODF分析[M].沈阳:东北工学院,1986.
【6】Jonas J J,Urabe T.Oriented nucleation and selective growth during the annealing of IF steal[C]//Proc Int Forum on Physical Metallurgy of IF steals.Tokyo:ISIJ,1994:77-94.
【7】Vatne H E,Daaland O.On the formation of cube texture in aluminum[J].Mater Sci Forum,1994(10):1087-1094.
【8】Kohno M,Muraki M,Kawano M,et al.Deformation microtexture and recrystallizd orientations in non-oriented electrical steel observed by high-resolution EBSD[J].Mater Sci Forum,2002(12):408-412.
【9】Hutchinson W B.Development and control of annealing texture in low-carbon steel[J].Int Met Rev,1984,29(1):25-33.
【10】胡卓超,蒋奇武,赵 骧,等.预回复对08Al深冲钢板再结晶组织及织构的影响[J].东北大学学报,2001,22:146-149.
【2】ZHANG De-fen,HU Zhuo-chao,ZUO Liang,et al.Evolution of textures during rolling and annealing of 3004 aluminium alloy[J].Journal of Nort Heastern University,2002,23(8):786-789.
【3】武保林,刘明玲,左良,等.Ti-15V-3Cr-3Sn-3Al板材织构与组织分析[J].材料工程,1997(增刊):41-43.
【4】沈桂琴,张庆玲,刘新华,等.Ti-15V-3Cr-3Sn-3Al合金板材的再结晶与织构特征[J].航空工艺技术,1996(6):18-20.
【5】梁志德,徐家桢,王福.织构材料的三维取向分析术——ODF分析[M].沈阳:东北工学院,1986.
【6】Jonas J J,Urabe T.Oriented nucleation and selective growth during the annealing of IF steal[C]//Proc Int Forum on Physical Metallurgy of IF steals.Tokyo:ISIJ,1994:77-94.
【7】Vatne H E,Daaland O.On the formation of cube texture in aluminum[J].Mater Sci Forum,1994(10):1087-1094.
【8】Kohno M,Muraki M,Kawano M,et al.Deformation microtexture and recrystallizd orientations in non-oriented electrical steel observed by high-resolution EBSD[J].Mater Sci Forum,2002(12):408-412.
【9】Hutchinson W B.Development and control of annealing texture in low-carbon steel[J].Int Met Rev,1984,29(1):25-33.
【10】胡卓超,蒋奇武,赵 骧,等.预回复对08Al深冲钢板再结晶组织及织构的影响[J].东北大学学报,2001,22:146-149.
相关信息