固溶温度和时间对ZL114A合金组织的影响
Influence of Solution Temperature and Time on Microstructure of ZL114A Alloy
摘 要
通过金相分析、动力学分析等方法,研究了固溶温度和固溶时间对ZL114A合金共晶硅形态的影响.结果表明:固溶温度对共晶硅的粒化过程有很大的影响,在不产生过烧时,温度越高共晶硅的粒化速率越快、粒化程度越彻底;固溶时共晶分枝和凹槽处首先熔断,并且端部钝化逐渐圆整;ZL114A合金在550 ℃×10 h固溶时的硅相形态最为理想.
固溶处理
组织
ZL114A aluminium alloy
solution treatment
microstructure
Abstract
Metallographic analysis and diffusion kinetics analysis were used to investigate the contribution of solution temperature and time to eutectic Si morphology of ZL114A alloy in the solution treatment process.The results indicate that the solution temperature is a significant influence factor on the process of eutectic Si spheroidization.Spheroidization degree of eutectic Si increases with the increase of solution temperature.As long as the temperature is below the overheat temperature,the divarication and neck section of eutectic Si break up firstly during solution treatment,and the Si phase is gradually passivated and rounded.The optimal Si morphology of ZL114A alloy was obtained after 550 ℃×10 h solution treatment.
中图分类号 TG146
所属栏目 试验研究
基金项目 广西科技开发计划资助项目(桂科能04430011-1)
收稿日期 2007/11/2
修改稿日期 2008/3/16
网络出版日期
作者单位点击查看
备注李卫超(1980-),男,黑龙江绥化人,硕士研究生.
引用该论文: LI Wei-chao,ZOU Yong-zhi,ZENG Jian-min. Influence of Solution Temperature and Time on Microstructure of ZL114A Alloy[J]. Materials for mechancial engineering, 2008, 32(11): 25～27
李卫超,邹勇志,曾建民. 固溶温度和时间对ZL114A合金组织的影响[J]. 机械工程材料, 2008, 32(11): 25～27
被引情况:
【1】李美春,邓运来,唐建国,万里,张新明, "不同时间固溶后6061铝合金中厚板的组织、性能及表面残余应力",机械工程材料 38, 39-45(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】宁爱林,曾苏民,蒋寿生.7A04铝合金高温固溶的微观组织和力学性能[J].轻合金加工技术,2005,33(5):48-50.
【2】宛农,董建新,谢锡善.AlSi7Mg 系铝合金组织的热力学分析[J].特种铸造及有色合金,2005,25(6):378-380.
【2】宛农,董建新,谢锡善.AlSi7Mg 系铝合金组织的热力学分析[J].特种铸造及有色合金,2005,25(6):378-380.
相关信息