轴承钢生产中的钡合金脱氧工艺
Barium Alloy Deoxidation Technique of Bearing Steel
摘 要
为提高GCr15轴承钢的质量,在生产中采用钢包精炼炉进行钡合金脱氧,并将此工艺生产的钢与钢包精炼炉和真空精炼炉用铝脱氧的钢进行了夹杂物对比分析和疲劳寿命对比试验.结果表明：钡合金脱氧钢的疲劳寿命高于相同氧含量真空和非真空铝脱氧钢的,钢中的夹杂物细小均匀,呈弥散分布,并消除了点状夹杂物;喂钡合金线的脱氧效果优于直接加入钡合金块的,其疲劳寿命最高,最终氧含量达到7 mg·kg-1.
轴承钢
钡合金
疲劳寿命
deoxidation
bearing steel
barium alloy
fatigue life
Abstract
In order to improve the quality of GCr15 bearing steel,barium alloy deoxidation was applied in refined-smelting ladle furnace during the producing process.Inclusions and fatigue life of the steels deoxidated with barium alloy were compared with those of the steels deoxidated with aluminum in refined-smelting ladle furnace and vacuum refining furnace.The results show that the fatigue life of the steels deoxidated with barium alloy was higher than that of the steels deoxidated with aluminum,and inclusions of the former were more homogeneous,smaller,more disperse and without punctual inclusions.The deoxidation effect of feeding barium alloy wire was better than that of the direct adding barium alloy block,and the finally gained steels with oxygen content of 7 mg·kg-1 had the highest fatigue life.
中图分类号 TG146.1
所属栏目 试验研究
基金项目 青海省科技攻关项目(2006-G-106)
收稿日期 2008/2/12
修改稿日期 2008/12/31
网络出版日期
作者单位点击查看
备注铁生年(1965-),男,青海民和人,教授.
引用该论文: TIE Sheng-nian,WANG Zhong-ying,CHEN Lie,LI Xing,LI Yun-jun. Barium Alloy Deoxidation Technique of Bearing Steel[J]. Materials for mechancial engineering, 2009, 33(2): 32～34
铁生年,王忠英,陈列,李星,李昀珺. 轴承钢生产中的钡合金脱氧工艺[J]. 机械工程材料, 2009, 33(2): 32～34
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Lund T,Akesson J.Cleanliness Requirements on Rolling BearingSteels[C]//.Proceedings of the Third International Conference on Cleansteel.Hungary:[s.n],1986:209-213.
【2】Cogne J Y,Heritier B,Monnot J.Cleanness and Fatigue Life of Bearing Steels[C]//Proceedings of the Third International Conference on Cleansteel,Hungary:[s.n],1986:26-31.
【3】朱应波.国外弹簧钢生产技术[M].北京:冶金工业出版社,1993.
【4】王忠英,于桂玲.60Si2Mn(A)弹簧钢的脱氧工艺[J].钢铁研究学报,2003,15(1):1-4.
【5】王忠英.钡系合金处理轴承钢的工艺和理论研究[D].北京:北京科技大学,1998.
【6】颜根发.含硅钡系合金取代铝脱氧的几个理论问题[J].华东冶金学院学报,1997,14(3):233.
【7】付云峰,徐德祥,陆佰亮.国内轴承钢的生产现状和发展[J].特殊钢,2002,23(6):30.
【2】Cogne J Y,Heritier B,Monnot J.Cleanness and Fatigue Life of Bearing Steels[C]//Proceedings of the Third International Conference on Cleansteel,Hungary:[s.n],1986:26-31.
【3】朱应波.国外弹簧钢生产技术[M].北京:冶金工业出版社,1993.
【4】王忠英,于桂玲.60Si2Mn(A)弹簧钢的脱氧工艺[J].钢铁研究学报,2003,15(1):1-4.
【5】王忠英.钡系合金处理轴承钢的工艺和理论研究[D].北京:北京科技大学,1998.
【6】颜根发.含硅钡系合金取代铝脱氧的几个理论问题[J].华东冶金学院学报,1997,14(3):233.
【7】付云峰,徐德祥,陆佰亮.国内轴承钢的生产现状和发展[J].特殊钢,2002,23(6):30.
相关信息