在役45钢构件半埋藏裂纹的电磁热止裂
Crack Arrest of Half-embedding Cracks of In-service 45 Steel Component by Electromagnetic Heating
摘 要
应用自制的ZL-2超强脉冲电流发生装置,对带有半埋藏裂纹的45钢拉伸试样进行了拉伸载荷作用下的脉冲放电电磁热止裂;对止裂前后的拉伸试样通过微机控制电子万能试验机进行了三点弯曲试验,并对止裂前后裂尖附近的显微组织进行了对比分析.结果表明:电磁热止裂后,裂纹尖端瞬时熔化、钝化,达到了裂纹止裂的目的;在裂纹尖端附近的组织出现了细化,电磁热止裂后试样所能承受的最大弯曲力和抗弯强度分别较止裂前提高了约23%和25%.
裂纹止裂
弯曲性能
pulse current discharge
crack arrest
bend property
Abstract
45 steel tensile specimens with half-embedding cracks were used to perform pulse discharge crack arrest experiment using a self-made ZL-2 super pulse current generation device. The three-point bending test was carried on the tensile specimens before and after the crack arrest using a computer control electronic universal testing machine. The microstructure near the crack tip was analyzed. The results show that the crack tip was instantly melt and dulled after pulse current discharge,resulting in crack arrest. The microstructure around the crack tip was refined. The maximum bending force and bending strength of specimens after crack arrest was improved by 23% and 25% compared specimens before arack arrest respectively.
中图分类号 O482.6 O346.1
所属栏目 试验研究
基金项目 国家自然科学基金资助项目(50675190)
收稿日期 2008/3/13
修改稿日期 2008/9/18
网络出版日期
作者单位点击查看
备注刘喜平(1957-),男,山东邹平人,教授,硕士.
引用该论文: LIU Xi-ping,ZHANG Yan-ling,FU Yu-ming. Crack Arrest of Half-embedding Cracks of In-service 45 Steel Component by Electromagnetic Heating[J]. Materials for mechancial engineering, 2009, 33(4): 32～34
刘喜平,张燕玲,付宇明. 在役45钢构件半埋藏裂纹的电磁热止裂[J]. 机械工程材料, 2009, 33(4): 32～34
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】BAI Xiang-zhong,FU Yu-ming. Advances in research on electromagnetic heating effects to stop crack propagation in metal components[J].International Journal of Nolinear Science and Numerical Simulation,2003,9(1):65-77.
【2】BAI Xiang-zhong,FU Yu-ming,GAO Dian-kui. Experimental research on electromagnetic heating effects to stop crack propagation in metal components[C]//The 3rd International Conference on Experimental Mechanics. Beijing: [n.l.],2001.
【3】BAI Xiang-zhong,FU Yu-ming. Temperature field near crack tip in a current-carrying plate under the repeated action of pulse current[J].International Journal of Nolinear Science and Numerical Simulation,2003,9(1):46-49.
【4】张宏图,陈易之.固体形变与断裂[M].北京:高等教育出版社,1989:348-400.
【5】FU Yu-ming,ZHENG Li-juan. Application of the fluid mechanics in analysis on the current field when crack arrest using pulse current discharge[C]//Proceedings of ISFP′2007:5th International Symposium on Fluid Power Transmission and Control,2007:1052-1053.
【6】高殿奎,付宇明,白象忠.GCr15凹模淬火裂纹止裂处的显微组织分析[J].金属学报,2001,37(2):135-138.
【2】BAI Xiang-zhong,FU Yu-ming,GAO Dian-kui. Experimental research on electromagnetic heating effects to stop crack propagation in metal components[C]//The 3rd International Conference on Experimental Mechanics. Beijing: [n.l.],2001.
【3】BAI Xiang-zhong,FU Yu-ming. Temperature field near crack tip in a current-carrying plate under the repeated action of pulse current[J].International Journal of Nolinear Science and Numerical Simulation,2003,9(1):46-49.
【4】张宏图,陈易之.固体形变与断裂[M].北京:高等教育出版社,1989:348-400.
【5】FU Yu-ming,ZHENG Li-juan. Application of the fluid mechanics in analysis on the current field when crack arrest using pulse current discharge[C]//Proceedings of ISFP′2007:5th International Symposium on Fluid Power Transmission and Control,2007:1052-1053.
【6】高殿奎,付宇明,白象忠.GCr15凹模淬火裂纹止裂处的显微组织分析[J].金属学报,2001,37(2):135-138.
相关信息