压缩机连杆断裂原因
Fracture Reason of the Compressor Connecting Rod
摘 要
通过宏观检查、显微组织观察、化学成分分析、力学性能试验和断口分析等方法,对天然气压缩机连杆的断裂原因进行分析.结果表明:压缩机连杆的失效形式为疲劳断裂;断裂的主要内因是锻造后热处理工艺不当,导致材料的屈服强度和抗拉强度降低;外因是连杆在工作过程中承受循环应力作用,由于材料强度降低,就会在应力集中部位——螺孔、螺纹底径处萌生显微裂纹,并随着裂纹的扩展而发生疲劳断裂.
疲劳断裂
热处理
压缩机
connecting rod
fatigue fracture
heat treatment
compressor
Abstract
Fracture reason of the compressor connecting rod was analyzed by means of macro observation,optical microscope,chemical analysis,mechanical test and fracture analysis. The results show that failure model of the rod was fatigue fracture. The improper heat treatment process resulted in the decrease of yield strength and tensile strength of the rod. Micro-crack initiated at the boot of screw thread because of high stress comcentration during working process,propagated due to cyclic loading and finally caused the fatigue rupture of the rod.
中图分类号 TG115.21
所属栏目 失效分析
基金项目
收稿日期 2008/4/15
修改稿日期 2008/11/2
网络出版日期
作者单位点击查看
备注宋文明(1975-),男,河北邯郸人,工程师,硕士.
引用该论文: SONG Wen-ming,ZHANG Yu-fu,ZHANG Jin-wei,YANG Gui-rong,ZHONG Yan-ping,MA Ying,HAO Yuan. Fracture Reason of the Compressor Connecting Rod[J]. Materials for mechancial engineering, 2009, 33(4): 64～66
宋文明,张玉福,张金伟,杨贵荣,钟彦平,马颖,郝远. 压缩机连杆断裂原因[J]. 机械工程材料, 2009, 33(4): 64～66
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】崔约贤.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998.
【2】胡光立.钢的热处理(原理和工艺)[M].西安:西北工业大学出版社,1993.
【3】机械工业部武汉材料保护研究所,机械工业部上海材料研究所.钢铁化学热处理金相图谱[M].北京:机械工业出版社,1980.
【2】胡光立.钢的热处理(原理和工艺)[M].西安:西北工业大学出版社,1993.
【3】机械工业部武汉材料保护研究所,机械工业部上海材料研究所.钢铁化学热处理金相图谱[M].北京:机械工业出版社,1980.
相关信息