Effect of Strain Rate on Deformation Induced Ferrite Transformation of Q235 Steel
摘 要
使用Gleeble 3500型热模拟试验机在850 ℃下对Q235钢进行压缩变形,研究了应变速率对Q235钢形变诱导铁素体相变的影响.结果表明:在较低的应变速率( 0.01 s-1)下,无法得到大量的形变诱导铁素体;而在较高的应变速率( >5 s-1)下,可以得到大量的形变诱导铁素体;随着应变速率的增大,变形后显微组织也逐渐变得更加均匀细小;应变速率越高,越容易发生形变诱导铁素体相变.
Abstract
Influence of strain rate on deformation induced ferrite transformation for Q235 steel was examined with Gleeble 3500 thermal simulator at 850 ℃.The results show that a lot of deformation induced ferrite could not be obtained at low strain rate (0.01 s-1).However,when the strain rate increased to higher than 5 s-1,the deformation induced ferrite could be found.The microstructure changed to be uniform and refine with increasing strain rate.The higher the strain rate was,the easier the formation of the deformation induced ferrite transformation was.
中图分类号 TG335
所属栏目 试验研究
基金项目
收稿日期 2008/4/16
修改稿日期 2009/2/13
网络出版日期
作者单位点击查看
备注吴建华(1964-),女,辽宁沈阳人,副教授,高级工程师,学士.
引用该论文: WU Jian-hua. Effect of Strain Rate on Deformation Induced Ferrite Transformation of Q235 Steel[J]. Materials for mechancial engineering, 2009, 33(5): 12~13
吴建华. 应变速率对Q235钢形变诱导铁素体相变的影响[J]. 机械工程材料, 2009, 33(5): 12~13
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨平,郝广瑞,孙祖庆.低碳钢中超细铁素体的长大倾向[J].北京科技大学学报,2002,24(5):519-524.
【2】胡安民,孙祖庆.低碳钢形变强化相变的组织细化[J].材料研究学报,2001,15(2):171-174.
【3】SUN Q Z,YANG W Y,QI J J,et al.Deformation enhanced transformation and dynamic recrystallization of ferrite in a low carbon steel during multipass hot deformation[J].Materials Science and Engineering A,2002,334:201-206.
【4】HUANG Y D,YANG Y W,SUN Z Q.Formation of ultrafine grained ferrite in low carbon steel by heavy deformation in ferrite or dual phase region[J].Journal of Materials Processing and Technology,2003,134:19-25.
【5】杜林秀,高彩茹,张彩碚,等.低碳钢应变诱导铁素体相变发生的温度条件[J].金属学报,2002,38(10):1031-1036.
【2】胡安民,孙祖庆.低碳钢形变强化相变的组织细化[J].材料研究学报,2001,15(2):171-174.
【3】SUN Q Z,YANG W Y,QI J J,et al.Deformation enhanced transformation and dynamic recrystallization of ferrite in a low carbon steel during multipass hot deformation[J].Materials Science and Engineering A,2002,334:201-206.
【4】HUANG Y D,YANG Y W,SUN Z Q.Formation of ultrafine grained ferrite in low carbon steel by heavy deformation in ferrite or dual phase region[J].Journal of Materials Processing and Technology,2003,134:19-25.
【5】杜林秀,高彩茹,张彩碚,等.低碳钢应变诱导铁素体相变发生的温度条件[J].金属学报,2002,38(10):1031-1036.
相关信息