Microstructure and Properties of Cu-Zr Alloy Prepared by Mechanical Alloying and Cold Pressing and Sintering
摘 要
采用机械合金化结合冷压烧结的方法制备了不同锆含量的铜-锆合金,用X射线衍射仪和扫描电镜等对制备的复合粉体进行了表征,并研究了球磨时间、烧结温度和保温时间、锆含量等因素对合金电阻率、硬度及抗弯强度的影响.结果表明:随着球磨时间的延长,复合粉体的主衍射峰强度逐渐降低,而铜-锆金属间化合物的衍射峰强度逐渐增加,颗粒由片状转变为近球状,而烧结后制得合金的电阻率和硬度逐渐升高;提高烧结温度和保温时间可以使合金的导电性能提高,但硬度下降;随着锆含量的增加,合金的电阻率、硬度及抗弯强度均不断增加.
Abstract
Cu-Zr alloys with different Zr content were prepared by mechanical alloying and cold pressing and sintering method,and the prepared composite powders were characterized using XRD and TEM.The effects of milling time,sintering temperature,soaking time and Zr content on the electrical resistivity,hardness and bending strength of the Cu-Zr alloys were investigated.The results show that with the increase of milling time,the main diffraction peaks intensity of the composite powders was reduced,diffraction peak intensity of Cu-Zr intermetallics was increased,the shape of the grains changed from sheet to approximative ball,and the electrical resistivity and hardness of the sintered alloy both increased gradually.The electrical conductivity of the alloy were increased by increasing sintering temperature and prolonging soaking time,but hardness of the alloy were reduced.With the increase of Zr content,electrical resistivity,hardness and bending strength of the Cu-Zr alloy all increased continuously.
中图分类号 TB331 TF12
所属栏目 材料性能及其应用
基金项目 安徽省“十五”二期科技攻关项目(040020392);合肥市重点科技攻关项目(20051044);安徽省自然科学基金资助项目(070414180)
收稿日期 2008/2/23
修改稿日期 2009/2/5
网络出版日期
作者单位点击查看
备注任阔(1982-),男,安徽阜阳人,硕士研究生.
引用该论文: REN Kuo,ZHENG Zhi-xiang,WU Yu-cheng,WANG De-bao,WANG Wen-fang,ZONG Yue. Microstructure and Properties of Cu-Zr Alloy Prepared by Mechanical Alloying and Cold Pressing and Sintering[J]. Materials for mechancial engineering, 2009, 33(5): 62~65
任阔,郑治祥,吴玉程,王德宝,王文芳,宗跃. 机械合金化结合冷压烧结制备铜-锆合金的组织与性能[J]. 机械工程材料, 2009, 33(5): 62~65
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王绍雄.铜和铜合金在电子工业中的新趋向[J].铜加工,1992(3):6-10.
【2】王隆寿.宝钢铬锆铜结晶器铜板的研制[J].冶金设备,1999,12(6):34-38.
【3】五十岚廉.引线框架材料[J].日本金属学会会报,1989(1):63-67.
【4】黄培云.粉末冶金原理[M].北京:冶金工业出版社,1995:111-118.
【5】黄新民,解挺.材料分析测试方法[M].北京:国防工业出版社,2006:37-43.
【6】MURTY B S,RANGANATHAN S.Novel material synthesis by mechanical alloying/milling[J].Int Mater Rev,1998,43(3):1-14.
【7】MAURICE D,COURTNEY T H.Modeling of mechanical alloying:part I.deformation coalescence,and fragmentation mechanisms[J].Metal Mater Trans A,1994,25(1):147-158.
【8】房晓勇,刘竞业,杨会静.固体物理学[M].哈尔滨:哈尔滨工业大学出版社,2004:157-159.
【2】王隆寿.宝钢铬锆铜结晶器铜板的研制[J].冶金设备,1999,12(6):34-38.
【3】五十岚廉.引线框架材料[J].日本金属学会会报,1989(1):63-67.
【4】黄培云.粉末冶金原理[M].北京:冶金工业出版社,1995:111-118.
【5】黄新民,解挺.材料分析测试方法[M].北京:国防工业出版社,2006:37-43.
【6】MURTY B S,RANGANATHAN S.Novel material synthesis by mechanical alloying/milling[J].Int Mater Rev,1998,43(3):1-14.
【7】MAURICE D,COURTNEY T H.Modeling of mechanical alloying:part I.deformation coalescence,and fragmentation mechanisms[J].Metal Mater Trans A,1994,25(1):147-158.
【8】房晓勇,刘竞业,杨会静.固体物理学[M].哈尔滨:哈尔滨工业大学出版社,2004:157-159.
相关信息