摘 要
采用电刷镀技术在不同表面粗糙度的W18Cr4V高速钢基体上制备了纳米PTFE和纳米WC颗粒增强的镍基复合镀层,采用扫描电镜对纳米复合镀层的表面和截面形貌进行了观察,研究了基体表面粗糙度对纳米复合镀层耐磨性、耐蚀性和结合强度的影响.结果表明:随着基体表面粗糙度的减小,纳米复合镀层的表面更加平整致密,组织更加细小均匀,镀层厚度减小,镀层中的裂纹数量减少,镀层的耐磨性、耐蚀性和结合强度均得到明显提高.
Abstract
PTFE and WC nano particles strengthened nickle base nano composite coatings were prepared by electro-brush plating on W18Cr4V high speed steels with different surface roughnesses.The morphology of surface and cross-section of the nano composite coatings was studied by SEM and the effect of surface roughness of substrate on the wear resistance,corrosion resistance and bind strength of the nano composite coatings were studied.The results show that with the decrease of the substrate surface roughness,surface of the nano composite coatings became smootner and denser,the microstructure became finer and more uniform,the coatings thickness reduced,cracks number decreased,and the wear resistance,corrosion resistance and bind strength were obviously improved.
中图分类号 TG154.5
所属栏目 试验研究
基金项目 上海市科委纳米专项资助项目(0552nm035);上海市重点学科建设项目(J51402)
收稿日期 2008/4/23
修改稿日期 2009/3/9
网络出版日期
作者单位点击查看
备注周细应(1964-),男,江西南昌人,副教授,硕士.
引用该论文: ZHOU Xi-ying,YAN Min-jie. Influence of Surface Roughness of Substrates on Microstructure and Properties of Nano Composite Coatings[J]. Materials for mechancial engineering, 2009, 33(6): 22~24
周细应,严敏杰. 基体表面粗糙度对纳米复合镀层组织及性能的影响[J]. 机械工程材料, 2009, 33(6): 22~24
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王为,郭鹤桐.纳米复合镀技术[J].化学通报,2003(3):178-183.
【2】DEREK V.An update on brush plating[J].Metal Finishing,2002(7):18-20.
【3】蒋斌,徐滨士,董世运,等.热处理对n-ZrO2/Ni复合刷镀层接触疲劳性能的影响[J].金属热处理,2003,28(9):22-25.
【4】ZHOU Xi-ying,QIAN Shi-qiang,LI Wei-hong,et al.Microstructure and behaviors of nano composite coatings[J].材料热处理学报,2004,25(5):1271-1274.
【5】马叙,姚素薇,张卫国.Fe-W-Al2O3纳米复合镀层的结构及其耐磨性[J].机械工程材料,2006,30(6):83-86.
【6】王晋春,程旭东,李丹虹,等.Ni-W-ZrO2纳米复合电镀工艺的研究[J].腐蚀与防护,2005,26(8):338-341.
【7】韦习成,李健,袁成清.磁控溅射TiN界面结合强度的压痕法测试[J].摩擦学学报,2000,20(3):229-230.
【2】DEREK V.An update on brush plating[J].Metal Finishing,2002(7):18-20.
【3】蒋斌,徐滨士,董世运,等.热处理对n-ZrO2/Ni复合刷镀层接触疲劳性能的影响[J].金属热处理,2003,28(9):22-25.
【4】ZHOU Xi-ying,QIAN Shi-qiang,LI Wei-hong,et al.Microstructure and behaviors of nano composite coatings[J].材料热处理学报,2004,25(5):1271-1274.
【5】马叙,姚素薇,张卫国.Fe-W-Al2O3纳米复合镀层的结构及其耐磨性[J].机械工程材料,2006,30(6):83-86.
【6】王晋春,程旭东,李丹虹,等.Ni-W-ZrO2纳米复合电镀工艺的研究[J].腐蚀与防护,2005,26(8):338-341.
【7】韦习成,李健,袁成清.磁控溅射TiN界面结合强度的压痕法测试[J].摩擦学学报,2000,20(3):229-230.
相关信息