Friction and Wear Properties of CuTeSeFe Alloy under Dry Sliding Condition
摘 要
利用环-盘式摩擦磨损试验机研究了铜碲硒铁合金的干摩擦磨损行为,分析了载荷和摩擦速度等参数对该合金摩擦磨损性能的影响,并用扫描电子显微镜对磨损形貌进行了观察.结果表明:铜碲硒铁合金的摩擦因数随载荷的增加变化不大,但随摩擦速度的增加而明显增大;合金的磨损率随载荷和摩擦速度的增加均增大;在轻载低速条件下,合金的磨损机制以犁削磨损和粘着磨损为主;在重载高速条件下,磨粒磨损和粘着磨损加剧.
Abstract
The friction and wear behavior of CuTeSeFe alloy as well as the effects of load and sliding speed on the friction and wear properties of the alloy under dry sliding conditions were investigated by ring-disc friction and wear tester.The worn surface morphologies were observed by SEM.The results show that with the increase of load the friction coefficient of the alloy scarcely changed,but it increased with the increase of sliding speed.The wear rate of the alloy increased with the increase of load and sliding speed.Plough wear and adhesive wear were the main wear mechanism of the alloy at low loads and low sliding speed,and abrasive wear and adhesive wear were aggravated at high sliding speed and heavy loads.
中图分类号 TG146.1
所属栏目 材料性能及其应用
基金项目
收稿日期 2008/5/4
修改稿日期 2008/12/29
网络出版日期
作者单位点击查看
备注薛云(1965-),女,浙江浦江人,讲师,硕士.
引用该论文: XUE Yun. Friction and Wear Properties of CuTeSeFe Alloy under Dry Sliding Condition[J]. Materials for mechancial engineering, 2009, 33(6): 90~92
薛云. 铜碲硒铁合金的干摩擦磨损性能[J]. 机械工程材料, 2009, 33(6): 90~92
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王爱群,徐瑞,迟长志.铸造铝青铜的摩擦特性与机械性能[J].辽宁工程技术大学学报,2000,19(1):87-89.
【2】徐祖豪,张修庆,邓鉴棋.热处理工艺对高强高导Cu-Cr-V-Zr-RE合金性能的影响[J].热加工工艺,2007,36(18):46-49.
【3】徐建林,喇培清,陈超.铸造铝青铜合金Cu-14Al-4Fe-Mn的摩擦磨损性能[J].摩擦学学报,2004,24(5):438-442.
【4】高化伟.CuAlBi合金摩擦磨损性能的研究[J].热加工工艺,2007,36(10):25-27.
【5】高红霞,刘建秀,朱茹敏.铜基粉末冶金列车闸瓦材料的摩擦磨损性能研究[J].材料科学与工程学报,2005,23(6):871-874.
【6】车建明.炭纤维增强铜基复合材料摩擦磨损性能同其磨损表面形貌相关性研究[J].摩擦学学报,2004,24(2):144-147.
【7】支龙,王耀华,谭业发.铝青铜热喷涂层/GCr15钢干摩擦磨损性能[J].机械工程材料,2005,29(5):52-54.
【8】王观民,张永振,杜三明.两种不同气氛下钢铜摩擦副摩擦磨损特性研究[J].热加工工艺,2006,35(24):8-11.
【9】浩宏奇,丁华东,李雅文.石墨含量对铜基材料摩擦磨损性能的影响[J].中国有色金属学报,1997,7(3):120-123.
【2】徐祖豪,张修庆,邓鉴棋.热处理工艺对高强高导Cu-Cr-V-Zr-RE合金性能的影响[J].热加工工艺,2007,36(18):46-49.
【3】徐建林,喇培清,陈超.铸造铝青铜合金Cu-14Al-4Fe-Mn的摩擦磨损性能[J].摩擦学学报,2004,24(5):438-442.
【4】高化伟.CuAlBi合金摩擦磨损性能的研究[J].热加工工艺,2007,36(10):25-27.
【5】高红霞,刘建秀,朱茹敏.铜基粉末冶金列车闸瓦材料的摩擦磨损性能研究[J].材料科学与工程学报,2005,23(6):871-874.
【6】车建明.炭纤维增强铜基复合材料摩擦磨损性能同其磨损表面形貌相关性研究[J].摩擦学学报,2004,24(2):144-147.
【7】支龙,王耀华,谭业发.铝青铜热喷涂层/GCr15钢干摩擦磨损性能[J].机械工程材料,2005,29(5):52-54.
【8】王观民,张永振,杜三明.两种不同气氛下钢铜摩擦副摩擦磨损特性研究[J].热加工工艺,2006,35(24):8-11.
【9】浩宏奇,丁华东,李雅文.石墨含量对铜基材料摩擦磨损性能的影响[J].中国有色金属学报,1997,7(3):120-123.
相关信息