洗衣机用自攻螺钉的断裂分析
Fracture Failure Analysis of Tapping Screw Used for Washing Machine
摘 要
采用原子发射光谱仪、显微硬度计、光学显微镜、扫描电子显微镜和能谱仪等对洗衣机用PH-INT-PC 4×14.5自攻螺钉的断裂原因进行了分析.结果表明:螺钉断裂是由于在酸洗、电镀过程中造成的渗氢及随后去氢处理不完全所引起的氢脆断裂;改进酸洗和电镀工艺,在镀锌后尽快进行去氢处理,可防止自攻螺钉发生氢脆断裂.
失效分析
氢脆
tapping screw
failure analysis
hydrogen embrittlement
Abstract
The fracture failure cause of the PH-INT-PC 4×14.5 tapping screw used for washing machine was analyzed by means of optical emission spectrometry,micro-hardness tester,optical microscopy,the scanning electron microscopy and energy dispersive X-ray spectrometer.The results show that the fracture of the screw was due to hydrogen embrittlement brought during manufacture process of both pickling and galvanizing of screw.In order to avoid the hydrogen embrittlement of the tapping screw,the technical parameters of the pickling and galvanizing have been modified,and hydrogen should be relieved after galvanizing as soon as possible.
中图分类号 TG146.1
所属栏目 失效分析
基金项目
收稿日期 2008/7/25
修改稿日期 2009/4/5
网络出版日期
作者单位点击查看
备注董秀文(1954-),男,辽宁大连人,研究员.
引用该论文: DONG Xiu-wen,LI Yan. Fracture Failure Analysis of Tapping Screw Used for Washing Machine[J]. Materials for mechancial engineering, 2009, 33(7): 72～74
董秀文,李岩. 洗衣机用自攻螺钉的断裂分析[J]. 机械工程材料, 2009, 33(7): 72～74
被引情况:
【1】骆 亍,宾远红,李培芬, "1018钢螺钉断裂失效分析",理化检验－物理分册 52, 281-283(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】肖纪美,曹楚南.材料腐蚀学原理[M].北京:化学工业出版社,2002:69-85.
【2】唐汝钧.机械工程材料测试手册：物理金相卷[M].沈阳:辽宁科学技术出版社,1999:844-846.
【3】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2004:197-206.
【4】李金桂.电镀氢脆故障及应对措施[J].材料保护,2006,39(8):51-53.
【5】张振赟.高强度紧固件镀锌中氢脆的产生环节及控制措施[J].材料保护,2003,36(1):62-64.
【6】理查德.西森.紧固件的氢脆与电镀[J]紧固件技术,2002(2):23-26.
【2】唐汝钧.机械工程材料测试手册：物理金相卷[M].沈阳:辽宁科学技术出版社,1999:844-846.
【3】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2004:197-206.
【4】李金桂.电镀氢脆故障及应对措施[J].材料保护,2006,39(8):51-53.
【5】张振赟.高强度紧固件镀锌中氢脆的产生环节及控制措施[J].材料保护,2003,36(1):62-64.
【6】理查德.西森.紧固件的氢脆与电镀[J]紧固件技术,2002(2):23-26.
相关信息