洗衣机不锈钢滚桶开裂失效分析
Cracking Failure Analysis of Stainless Steel Washer Roller
摘 要
通过光学显微镜、扫描电镜、能谱仪等手段对1Cr17不锈钢洗衣机滚桶开裂原因进行了分析.结果表明:其开裂性质为沿晶应力腐蚀开裂;开裂处晶界存在第二相是滚桶开裂的内因,母材成分中铬含量偏低降低了材料的抗蚀性能及韧性,开裂处存在内应力是开裂的外因.
不锈钢滚桶
开裂
贫铬
晶界
washer
stainless steel roller
cracking
Cr depletion
grain boundary
Abstract
The cracking failure of 1Cr17 stainless steel washer roller was investigated by means of OM,SEM and EDS.The results show that the property was intergranular stress corrosion cracking.Second phase in the cracking grain boundary was the internal cause of the roller cracking.The Cr content in the base metal was low,which decreased the corrosion-resistance and toughness of the material.Stress in the cracking position was the external cause.
中图分类号 TG111.91
所属栏目 失效分析
基金项目 上海市重点学科建设资助项目(J51402);上海工程技术大学重点学科资助项目(xk0705)
收稿日期 2008/7/14
修改稿日期 2009/1/6
网络出版日期
作者单位点击查看
备注刘淑梅(1968-),女,山东烟台人,讲师,硕士.
引用该论文: LIU Shu-mei. Cracking Failure Analysis of Stainless Steel Washer Roller[J]. Materials for mechancial engineering, 2009, 33(8): 90～92
刘淑梅. 洗衣机不锈钢滚桶开裂失效分析[J]. 机械工程材料, 2009, 33(8): 90～92
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】涂铭旌,鄢文彬.机械零件失效分析与预防[M].北京:高等教育出版社,1993.
【2】于志强,张宏鹤,杨振国.送风机电机轴承外圈断裂失效分析[J].金属热处理,2007,32(7):74-76.
【3】张启君.3Cr13不锈钢传动轴表面产生细纹的原因分析[J].金属热处理,2006,31(5):80-83.
【4】唐世华,郝俊文,潘红良.膨胀干燥机加热夹套开裂原因分析[J].机械工程材料,2007,31(1):63-66.
【2】于志强,张宏鹤,杨振国.送风机电机轴承外圈断裂失效分析[J].金属热处理,2007,32(7):74-76.
【3】张启君.3Cr13不锈钢传动轴表面产生细纹的原因分析[J].金属热处理,2006,31(5):80-83.
【4】唐世华,郝俊文,潘红良.膨胀干燥机加热夹套开裂原因分析[J].机械工程材料,2007,31(1):63-66.
相关信息