Quenching Cracking Reason Analysis of Spring Using for Train Buffer
摘 要
某列车缓冲器弹簧在淬火后出现了纵向裂纹;利用化学成分分析、硬度检测、断口分析、夹杂物和显微组织分析等手段对弹簧淬火开裂原因进行了分析.结果表明:原材料组织中的带状偏析和沿轧制方向分布数量多且粗大的非金属夹杂物是弹簧淬火开裂的主要原因;夹杂物和带状偏析造成材料组织和性能均匀性变差,粗大的非金属夹杂物成为裂纹源,在组织应力的作用下,促进裂纹形成并迅速扩展成为沿轧制方向分布的淬火裂纹.
Abstract
The vertical-cracking on spring buffer of a train produced were found after quenching.Quenching cracking reason of the spring was analysis by using chemical compositions analysis,hardness test,facture analysis,inclusion and microstructure observation.The results show that the main reasons of the cracking were the thick,big and large amount of zonal segregation and large nonmetallic inclusions which were distributed in rolling direction of the materials during the quench hardening.The inlusion and the zonal segregation made the homogeneity of microstructure and properties get worse,the large nonmetallic inclusions became the crack region.The crack was formed and propagated as a function of structure strain.
中图分类号 TG146.1
所属栏目 失效分析
基金项目 国家科技支撑计划资助项目(2007BAE11B03);贵州省重大专题资助项目(2006-6029)
收稿日期 2008/7/12
修改稿日期 2009/5/21
网络出版日期
作者单位点击查看
备注杨刚(1983-),男,四川成都人,硕士研究生.
引用该论文: YANG Gang,LIANG Yi-long,ZOU Zhi-yong,TIAN Zhong-jian,DAI Yi. Quenching Cracking Reason Analysis of Spring Using for Train Buffer[J]. Materials for mechancial engineering, 2009, 33(8): 96~99
杨刚,梁益龙,邹志勇,田中健,戴毅. 列车缓冲器弹簧淬火开裂原因分析[J]. 机械工程材料, 2009, 33(8): 96~99
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郭任农.MT-2型货车缓冲器的装配和检验[J].铁道技术监督,2007(5):38-39.
【2】刘健,宋西平.45热轧圆钢顶锻开裂原因分析[J].机械工程材料,2008,32(10):67-70.
【3】王荣.弹簧座开裂原因分析[J].机械工程材料,2008,32(9):82-84.
【4】方杭玮,孙丹杰.弹簧钢中带状偏析对弹条金相组织的影响[J].工程建设与设计,2004(8):76-77.
【5】蒋生蕊.高碳钢马氏体亚结构的形成与相变开裂[J].金属学报,1986(5):A393-A402.
【2】刘健,宋西平.45热轧圆钢顶锻开裂原因分析[J].机械工程材料,2008,32(10):67-70.
【3】王荣.弹簧座开裂原因分析[J].机械工程材料,2008,32(9):82-84.
【4】方杭玮,孙丹杰.弹簧钢中带状偏析对弹条金相组织的影响[J].工程建设与设计,2004(8):76-77.
【5】蒋生蕊.高碳钢马氏体亚结构的形成与相变开裂[J].金属学报,1986(5):A393-A402.
相关信息