钕对Mg-5Zn-2Al合金显微组织和力学性能的影响
Effect of Nd on Microstructure and Mechanical Properties of Mg-5Zn-2Al Alloy
摘 要
利用光学显微镜、电子万能试验机、扫描电镜和X射线衍射仪等研究了不同含量的稀土元素钕(质量分数分别为0.3%,0.6%和0.9%)对铸态Mg-5Zn-2Al合金显微组织和力学性能的影响.结果表明:铸态Mg-5Zn-2Al合金主要由α-Mg基体相、τ-Mg32(Al,Zn)49相及AlNd相组成,并且AlNd相随着合金中钕含量的增加而增多;合金的力学性能随着钕含量的增加呈现先上升后下降的变化趋势,当钕含量为0.6%时,合金的抗拉强度达到最大,为204 MPa,合金的伸长率也达到最大值11.125%.
稀土元素
显微组织
力学性能
Mg-5Zn-2Al alloy
rare earth element
microstructure
mechanical property
Abstract
The influence of element Nd addition on the microstructure and mechanical properties of as-cast Mg-5Zn-2Al alloys ( with content of Nd was 0.3wt%,0.6wt% and 0.9wt% respectively) had been investigated by using metallographic microscope,electronic universal matrials testing machine,scanning electron microscopy and X-ray diffraction.The results show that,for the as-cast Mg-5Zn-2Al alloys,the main phases were α-Mg matrix phase,τ-Mg32(Al,Zn)49 phase and AlNd phase.With increasing the addition of Nd in the alloys,the amount of AlNd phase increased.The mechanical properties exhibited the trend of arising first and descending later.When the content of Nd was 0.3wt%,the tensile strength was the highest,with the value about 204 MPa.The elongation reached the highest,with the value about 11.125%.
中图分类号 TG146.22 TG146.4
所属栏目 试验研究
基金项目 甘肃省自然科学基金资助项目(3ZS062-B25-026);兰州理工大学博士基金资助项目(SB01200406)
收稿日期 2008/9/22
修改稿日期 2009/5/13
网络出版日期
作者单位点击查看
备注黄晓锋(1971-),男,吉林白城人,副教授.
引用该论文: HUANG Xiao-feng,CAO Xi-juan,ZHU Kai,TIAN Zai-you,LIANG Yan. Effect of Nd on Microstructure and Mechanical Properties of Mg-5Zn-2Al Alloy[J]. Materials for mechancial engineering, 2009, 33(10): 23～26
黄晓锋,曹喜娟,朱凯,田载友,梁燕. 钕对Mg-5Zn-2Al合金显微组织和力学性能的影响[J]. 机械工程材料, 2009, 33(10): 23～26
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王渠东,吕宜振,曾小勤,等.稀土在铸造合金中的应用[J].特种铸造及有色合金,1999,26(1):292-299.
【2】刘斌,刘顺华,金文中,等.稀土在镁合金中的作用与影响[J].上海有色金属,2003,24(1):27-30.
【3】贾振江,许春香,任洪涛,等.稀土元素Nd对AM50镁合金金相组织和力学性能的影响[J].铸造设备研究,2007,12(6):18-24.
【4】刘刚强,陈乐平,艾云龙.稀土Nd对ZM5合金组织于性能影响的研究[J].特种铸造及有色合金,2005,25(7):496-498.
【5】LA Yi-zhen,WANG Qu-dong,ZENG Xiao-qin,et al.Effects of rare earth on the microstructure properties and fracture behavior of Mg-Al alloys[J].Mater Sci Eng A,2000,A278:66-76.
【6】LI Y,JONES H.Effect of rare earth and silison additions on structure and properties of melt Mg-9Al -Zn alloy[J].Materials Science and Technology,1996,12(8):651-661.
【7】中山大学金属系.稀土物理化学常数[M].北京:冶金工业出版社,1978:115-117.
【8】WEI L Y.Development of microstructure in cast Mg-Al-rare earth alloys[J].Mater Sci Tech,1996,12(9):741-750.
【9】肖纪美,朱逢吾.材料能量学[M].上海:上海科学技术出版社,1999:79-81.
【10】高洪吾,胡晓菊,李长茂,等.RE元素Y和Nd对Mg-Al合金显微组织的影响[J].特种铸造及有色合金,2004(6):29-31.
【11】宋波,刘勇兵,安健,等.钕及固溶处理对AM60合金组织及力学性能的影响[J].铸造技术,2006,27(12):1299-1302.
【12】张波,杜文博,吴玉峰,等.Zr对铸造MgZn5Nd3.5合金组织和性能的影响[J].特种铸造及有色合金,2006,26(2):74-76.
【13】李萍.Nd对镁合金AZ91力学性能的影响[J].有色合金,2008,60(1):22-24.
【2】刘斌,刘顺华,金文中,等.稀土在镁合金中的作用与影响[J].上海有色金属,2003,24(1):27-30.
【3】贾振江,许春香,任洪涛,等.稀土元素Nd对AM50镁合金金相组织和力学性能的影响[J].铸造设备研究,2007,12(6):18-24.
【4】刘刚强,陈乐平,艾云龙.稀土Nd对ZM5合金组织于性能影响的研究[J].特种铸造及有色合金,2005,25(7):496-498.
【5】LA Yi-zhen,WANG Qu-dong,ZENG Xiao-qin,et al.Effects of rare earth on the microstructure properties and fracture behavior of Mg-Al alloys[J].Mater Sci Eng A,2000,A278:66-76.
【6】LI Y,JONES H.Effect of rare earth and silison additions on structure and properties of melt Mg-9Al -Zn alloy[J].Materials Science and Technology,1996,12(8):651-661.
【7】中山大学金属系.稀土物理化学常数[M].北京:冶金工业出版社,1978:115-117.
【8】WEI L Y.Development of microstructure in cast Mg-Al-rare earth alloys[J].Mater Sci Tech,1996,12(9):741-750.
【9】肖纪美,朱逢吾.材料能量学[M].上海:上海科学技术出版社,1999:79-81.
【10】高洪吾,胡晓菊,李长茂,等.RE元素Y和Nd对Mg-Al合金显微组织的影响[J].特种铸造及有色合金,2004(6):29-31.
【11】宋波,刘勇兵,安健,等.钕及固溶处理对AM60合金组织及力学性能的影响[J].铸造技术,2006,27(12):1299-1302.
【12】张波,杜文博,吴玉峰,等.Zr对铸造MgZn5Nd3.5合金组织和性能的影响[J].特种铸造及有色合金,2006,26(2):74-76.
【13】李萍.Nd对镁合金AZ91力学性能的影响[J].有色合金,2008,60(1):22-24.
相关信息