动态条件下Fe-24Mn-0.5C孪晶诱发塑性钢的断裂机制
Fracture Mechanism of Fe-24Mn-0.5C TWIP Steel under Dynamic Conditon
摘 要
对Fe-24Mn-0.5C孪晶诱发塑性钢进行了动态冲击拉伸试验,并采用扫描电镜、透射电镜等研究了该钢的断裂机制.结果表明:试验钢的抗拉强度为1 100 MPa,断后伸长率为50%;试验钢表现为典型的韧性断裂特征,断口主要由呈阶梯状的韧窝组成;其断裂机制为变形过程中塞积在晶界和孪晶界处的大量位错促使孔洞及裂纹的产生,继续变形则发生断裂.
动态拉伸
微孔洞
断裂机制
TWIP steel
dynamic tension
micro-void
fracture mechanism
Abstract
The fracture mechanism of Fe-24Mn-0.5C TWIP steel after dynamic impact tension was studied by using SEM and TEM.The results show that the tensile strength of the test steel was 1 100 MPa and rupture elongation was 50%.It showed typical ductile fracture characteristics.The fracture contained lots of stepladder dimples.The fracture mechanism was the formation of holes and cracks promoted by the dislocation piled up in grain and twin boundaries during the deformation process,and fracture would appear with further deformation.
中图分类号 TG111.91
所属栏目 试验研究
基金项目 先进钢铁材料技术国家工程研究中心项目(50671061)
收稿日期 2008/10/16
修改稿日期 2009/8/17
网络出版日期
作者单位点击查看
备注周小芬(1983-),女,江苏常州人,硕士研究生.
引用该论文: ZHOU Xiao-fen,FU Ren-yu,SU Yu,LI Lin. Fracture Mechanism of Fe-24Mn-0.5C TWIP Steel under Dynamic Conditon[J]. Materials for mechancial engineering, 2009, 33(11): 24～26
周小芬,符仁钰,苏钰,李麟. 动态条件下Fe-24Mn-0.5C孪晶诱发塑性钢的断裂机制[J]. 机械工程材料, 2009, 33(11): 24～26
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】CORNETTE D,CUGY P,HILDENBRAND A,et al.Super-high strength Fe-Mn TWIP steel of automotive[J].La Revue de Metallurgie,2005(12):905-918.
【2】韦习成.Si-Mn系相变诱发塑性钢的动态力学性能[D].上海:上海大学,2002.
【3】苏玉芹.金属塑性变形原理 [M].北京:冶金工业出版社,1995.
【4】张栋,钟培道.机械失效的实用分析 [M].北京:国防工业出版社,1997.
【2】韦习成.Si-Mn系相变诱发塑性钢的动态力学性能[D].上海:上海大学,2002.
【3】苏玉芹.金属塑性变形原理 [M].北京:冶金工业出版社,1995.
【4】张栋,钟培道.机械失效的实用分析 [M].北京:国防工业出版社,1997.
相关信息