Microstructure and Properties of TIG Welded Joint of Hot Rolled 410S Stainless Steel Plates
摘 要
通过对热轧410S不锈钢板材手工钨极氩弧焊(TIG)焊接接头的组织观察、无损检测、力学性能和耐晶间腐蚀性能试验,以及铁素体含量和显微硬度的测定,研究了热轧410S不锈钢板材TIG焊接接头的组织与性能.结果表明:采用TIG方法焊接410S不锈钢接头的抗拉强度不低于母材的,而且塑性良好;焊接接头的宏观形貌呈铸造粗大组织,并具有明显的外延生长特性;焊缝组织主要为柱状晶奥氏体+沿柱状晶分布的δ铁素体,δ铁素体体积分数为15%~20%;热影响区的马氏体在焊接热的作用下发生了M→γ→M相变,原处于晶界条带中细小的颗粒状马氏体被黑色的团块状马氏体所替代;该焊接接头的晶间腐蚀倾向按热影响区、母材、焊缝顺序依次降低.
Abstract
The microstructure and properties of TIG welded joint of hot rolled 410S stainless steel plates were studied by using metallographic microscopy,nondestructive examination (NDE),mechanical property testing and Huey test,ferrite content and microhardness measuraments.The results show that the tensile strength of TIG welded joint was not less than that of base-metals,and the ductility was fine.The macrograph of the weld joint exhibited coarse structure with epitaxial growth characteristic.Microstructure of weld joint was composed of columnar austenic grains and ferrite along the austenite.The ferrite volume fraction was 15%-20%.Martensite phase in HAZ created M→γ→M,fine particle martensite at grain boundaries was converted into black block martensite.The intergranular corrosion trend of the joint was HAZ > base material > weld seam.
中图分类号 TG113.25 TG142.71
所属栏目 材料性能及其应用
基金项目 甘肃省有色金属新材料重点实验室开放基金资助项目(SKL05011)
收稿日期 2008/10/14
修改稿日期 2009/5/24
网络出版日期
作者单位点击查看
备注杨瑞成(1946-),男,江苏宝应人,教授.
引用该论文: YANG Rui-cheng,MENG Wei,SHU Jun,HU Tian-lei. Microstructure and Properties of TIG Welded Joint of Hot Rolled 410S Stainless Steel Plates[J]. Materials for mechancial engineering, 2009, 33(11): 72~75
杨瑞成,孟威,舒俊,胡天雷. 热轧410S不锈钢板材钨极氩弧焊焊接接头的组织与性能[J]. 机械工程材料, 2009, 33(11): 72~75
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陆世英,张廷凯,杨长强,等.不锈钢[M].北京:原子能出版社,1995:122-124.
【2】张其枢,诸耀庭.不锈钢焊接[M].北京:机械工业出版社,2003:353-354.
【3】王宝森,马立,叶晓宁,等.12%Cr铁素体不锈钢的焊接热影响区组织特征[J].宝钢技术,2007(3):70-74.
【4】SEDAT K.The effect of the welding temperature on the weld ability in diffusion welding of martensite (AISI 420 )stainless steel with ductile cast iron[J].Journal of Materials Processing Technology,2007,186:33-36.
【5】TSAI M C.Phase transformation in AISI 410 stainless steel[J].Materials Science and Engineering A,2002,332:1-10.
【6】李神速.双回路EPR法测定奥氏体不锈钢的敏化[J].腐蚀科学与防护技术,2000,12(5):288-291.
【7】铃木春义,田春博.焊接金属学[M].严鸢飞,罗志昌,陈伯蠡,译.北京:机械工业出版社,1982:62-65.
【8】利波尔德,科特基.不锈钢焊接冶金学及焊接性[M].陈剑虹,译.北京:机械工业出版社,2008:8-11.
【9】肖纪美.不锈钢的金属学问题[M].北京:冶金工业出版社,2006:182-190.
【10】秦丽雁,董征东.用电化学方法测量不锈钢晶间腐蚀的敏感性[J].太钢科技,1991(3):80-86.
【2】张其枢,诸耀庭.不锈钢焊接[M].北京:机械工业出版社,2003:353-354.
【3】王宝森,马立,叶晓宁,等.12%Cr铁素体不锈钢的焊接热影响区组织特征[J].宝钢技术,2007(3):70-74.
【4】SEDAT K.The effect of the welding temperature on the weld ability in diffusion welding of martensite (AISI 420 )stainless steel with ductile cast iron[J].Journal of Materials Processing Technology,2007,186:33-36.
【5】TSAI M C.Phase transformation in AISI 410 stainless steel[J].Materials Science and Engineering A,2002,332:1-10.
【6】李神速.双回路EPR法测定奥氏体不锈钢的敏化[J].腐蚀科学与防护技术,2000,12(5):288-291.
【7】铃木春义,田春博.焊接金属学[M].严鸢飞,罗志昌,陈伯蠡,译.北京:机械工业出版社,1982:62-65.
【8】利波尔德,科特基.不锈钢焊接冶金学及焊接性[M].陈剑虹,译.北京:机械工业出版社,2008:8-11.
【9】肖纪美.不锈钢的金属学问题[M].北京:冶金工业出版社,2006:182-190.
【10】秦丽雁,董征东.用电化学方法测量不锈钢晶间腐蚀的敏感性[J].太钢科技,1991(3):80-86.
相关信息