冷轧钢板表面缺陷的形成原因
Formation Reason of Surface Defect on Cold Rolled Steel Sheet
摘 要
采用光学显微镜、扫描电镜、能谱仪等对冷轧钢板表面出现的大量长条状细线缺陷产生原因进行了分析.结果表明:出现大量的长条细线缺陷的原因是钢板在冷轧过程中被前几道次轧辊或输送辊辊道表面凸起物划伤,再经过后几道次继续轧制所致.
表面缺陷
划伤
cold rolled steel sheet
surface defect
scratch
Abstract
The reason for the plenty of scratch on the surface of the cold rolled steel sheet was analyzed with optical microscopy,scanning electron microscopy and energy disperse spectrometer.The results show that the steel sheet was scratched by the protuberance on the work roll of the former passes or the conveying table roller during the cold rolling and thus led to the formation of defects.
中图分类号 TG142
所属栏目 失效分析
基金项目 新疆维吾尔自治区高校科研计划科学研究重点项目(XJEDU2006I11)
收稿日期 2008/10/19
修改稿日期 2009/5/10
网络出版日期
作者单位点击查看
备注马正伟(1982-),男,山东临沂人,硕士研究生.
引用该论文: MA Zheng-wei,LIU Bing. Formation Reason of Surface Defect on Cold Rolled Steel Sheet[J]. Materials for mechancial engineering, 2009, 33(11): 90～92
马正伟,刘炳. 冷轧钢板表面缺陷的形成原因[J]. 机械工程材料, 2009, 33(11): 90～92
被引情况:
【1】井玉安,胡希达,臧晓明,覃毅,李春福, "热轧带钢还原冷轧后的表面及横截面形貌",机械工程材料 38, 60-64(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李兴东,刘宏民,李俊洪.冷轧钢板边包缺陷产生根源的工业实验[J].钢铁研究学报,2008,20(7):29-33.
【2】李丽霞,尹显东,王中和.冷轧薄板边部折印缺陷产生原因及解决措施[J].鞍钢技术,1997(3):20-23.
【3】何宇明,朱斌,陈文满,等.中厚板表面微裂纹成因及影响因素研究[J].钢铁,2006,41(1):36-39.
【4】郭太雄,钟声,贾斌,等.冷轧薄板表面条痕缺陷成因及预防[J].轧钢,2000,23(6):22-24.
【2】李丽霞,尹显东,王中和.冷轧薄板边部折印缺陷产生原因及解决措施[J].鞍钢技术,1997(3):20-23.
【3】何宇明,朱斌,陈文满,等.中厚板表面微裂纹成因及影响因素研究[J].钢铁,2006,41(1):36-39.
【4】郭太雄,钟声,贾斌,等.冷轧薄板表面条痕缺陷成因及预防[J].轧钢,2000,23(6):22-24.
相关信息