Effect of Sub-temperature Quenching on Microstructure and Mechanical Properties of 25MnV Steel
摘 要
采用正交组合回归设计试验方法研究了不同温度亚温淬火对25MnV钢抗拉强度和硬度的影响,分析了该钢亚温淬火后的组织.结果表明:25MnV钢经亚温淬火后,得到极细的板条状马氏体组织;830 ℃淬火时,马氏体板条之间分布着条状的铁素体;在810~830 ℃温度范围内,随淬火温度升高,该钢的强度和硬度升高,830 ℃亚温淬火的强度、硬度最好.
Abstract
The effect of sub-temperature quenching at different temperature on the tensile strength and hardness of 25MnV steel was investigated by orthogonal regressive principle.The microstructure of the steel after sub-temperature quenching was analyzed.The results indicate that the very fine lath martensite of 25MnV steel was obtained by sub-temperature quenching.The strip ferrite was distributed between martensite laths as the steel quenched at 830 ℃.In the temperature range of 810 to 830 ℃,the strength and hardness of the steel were increased along with the increasing of the quenching temperature.The best tensile strength and hardness could obtain in 25MnV steel when sub-temperature quenched at 830 ℃.
中图分类号 TG156
所属栏目 试验研究
基金项目 河南省自然科学基金资助项目(0511052600)
收稿日期 2008/11/13
修改稿日期 2009/8/10
网络出版日期
作者单位点击查看
备注李安铭(1955-),男,河南温县人,教授.
引用该论文: LI An-ming,WANG Hai-rui. Effect of Sub-temperature Quenching on Microstructure and Mechanical Properties of 25MnV Steel[J]. Materials for mechancial engineering, 2009, 33(12): 36~38
李安铭,王海瑞. 亚温淬火对25MnV钢显微组织和力学性能的影响[J]. 机械工程材料, 2009, 33(12): 36~38
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张太超.27SiMn钢临界温度淬火高温回火后的力学性能[J].金属热处理,2003(8):32-34.
【2】金麓,董建萍,王金统.27SiMn钢亚温淬火工艺研究[J].河北冶金,2003(5):45-46.
【3】HAN Jian-min,CUI Shi-hai.Dual phase heat treatment of low-alloy steel[J].J Iron&Stell Res,Int,2005,9:47-51.
【4】黄廷杰.40Cr钢强韧化处理后的力学性能[J].热加工工艺,2006,35(14):56-57.
【2】金麓,董建萍,王金统.27SiMn钢亚温淬火工艺研究[J].河北冶金,2003(5):45-46.
【3】HAN Jian-min,CUI Shi-hai.Dual phase heat treatment of low-alloy steel[J].J Iron&Stell Res,Int,2005,9:47-51.
【4】黄廷杰.40Cr钢强韧化处理后的力学性能[J].热加工工艺,2006,35(14):56-57.
相关信息