镁合金压铸机用高钴高铬热作模具钢的热处理工艺
Heat Treatment of High Cobalt and Chromium Hot-Work Die Steel Used in Magnesium Alloy Die-Casting Machine
摘 要
利用光学显微镜、扫描电镜、能谱仪和X射线衍射仪等研究了不同淬火和回火工艺对新型镁合金压铸机用X20CoCrWMoV10-9热作模具钢显微组织和硬度的影响,以确定其热处理工艺.结果表明:该钢较佳的热处理工艺为840 ℃×8 h退火预处理+1 100 ℃×1 h淬火+700 ℃×2 h回火;该钢经较佳工艺处理后,其显微组织由回火马氏体、金属间化合物μ相和合金碳化物M23C6、M6C组成;在1 100 ℃×1 h淬火后其硬度达到最大值51.5 HRC;在500~650 ℃回火时析出了较多弥散分布的金属间化合物和碳化物,具有较高的回火抗力和明显的二次硬化效应.
热处理
显微组织
二次硬化
hot-work die steel
heat treatment
microstructure
secondary hardening
Abstract
The effects of quenching and tempering processes on microstructure and hardness of X20CoCrWMoV10-9 hot-work die steel used in new magnesium alloy pressure die casting machine were studied by using the OM,SEM,EDS and XRD.Then the heat treatment process was determined.The results show that the optimized heat treatment of the steel was suggested that the steel was annealed at 840 ℃ for 8 h,then solution-treated at 1 100 ℃ for 1 h and oil quenched,followed by aged at 700 ℃ for 2 h.The microstructure of the steel treated with the process was consisted of tempered martensite,intermetallics μ phase,carbide M23C6 and M6C.The hardness of the steel reached to 51.5 HRC after quenched at 1 100 ℃ for 1 h.Due to the precipitation of intermetallics and alloy carbides in the steel during the tempering treatment at 550-650 ℃,the steel presented high tempering resistance.
中图分类号 TG146.1
所属栏目 新材料 新工艺
基金项目 广东省自然科学基金资助项目(07006483)
收稿日期 2008/9/19
修改稿日期 2009/9/14
网络出版日期
作者单位点击查看
备注高鹏(1985-),男,陕西洋县人,硕士研究生.
引用该论文: GAO Peng,LIU Jiang-wen,LUO Cheng-ping,LIU Zhi-jian. Heat Treatment of High Cobalt and Chromium Hot-Work Die Steel Used in Magnesium Alloy Die-Casting Machine[J]. Materials for mechancial engineering, 2009, 33(12): 66～69
高鹏,刘江文,罗承萍,刘志坚. 镁合金压铸机用高钴高铬热作模具钢的热处理工艺[J]. 机械工程材料, 2009, 33(12): 66～69
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】MORDIKE B L,EBERT T.Magnesium properties applications potential[J].Mater Sci Eng A,2001,102(1):37-45.
【2】刘树勋.力劲热室压铸机工作手册[M].北京:机械工业出版社,1999.
【3】彭程,刘树勋,李培杰,等.HDM钢热处理工艺研究[J].金属热处理,2002,27(5):3-6.
【4】刘树勋,李培杰,黄相全,等.高Co稀土热作模具钢析出相沉淀析出的研究[J].材料热处理学报,2002,23(3):15-19.
【5】TCHIZHIK A A,TCHIZHIK T A,TCHIZHIK ANNA A.Optimization of the heat treatment for steam and gas turbine parts manufactured from 9%-12% Cr steels[J].Journal of Materials Processing Technology,1998,77(1/3):226-232.
【6】章守华.合金钢[M].北京:冶金工业出版社,1981:178-179.
【7】孙刚,马志毅,曹毅,等.热作模具钢的合金化特点[J].拖拉机与农用运输车,2001(6):41-43.
【8】约·盖勒.工具钢[M].周倜武,丁立铭,译.北京:国防工业出版社,1983.
【9】余瑞瑛.固体与分子经验电子理论[J].科学通报,1978,23(4):217-218.
【10】李培杰,刘树勋,熊玉华,等.Co在Fe-Co-Cr系高合金钢中作用机制的电子理论[J].科学通报,2002,47(22):1690-1692.
【2】刘树勋.力劲热室压铸机工作手册[M].北京:机械工业出版社,1999.
【3】彭程,刘树勋,李培杰,等.HDM钢热处理工艺研究[J].金属热处理,2002,27(5):3-6.
【4】刘树勋,李培杰,黄相全,等.高Co稀土热作模具钢析出相沉淀析出的研究[J].材料热处理学报,2002,23(3):15-19.
【5】TCHIZHIK A A,TCHIZHIK T A,TCHIZHIK ANNA A.Optimization of the heat treatment for steam and gas turbine parts manufactured from 9%-12% Cr steels[J].Journal of Materials Processing Technology,1998,77(1/3):226-232.
【6】章守华.合金钢[M].北京:冶金工业出版社,1981:178-179.
【7】孙刚,马志毅,曹毅,等.热作模具钢的合金化特点[J].拖拉机与农用运输车,2001(6):41-43.
【8】约·盖勒.工具钢[M].周倜武,丁立铭,译.北京:国防工业出版社,1983.
【9】余瑞瑛.固体与分子经验电子理论[J].科学通报,1978,23(4):217-218.
【10】李培杰,刘树勋,熊玉华,等.Co在Fe-Co-Cr系高合金钢中作用机制的电子理论[J].科学通报,2002,47(22):1690-1692.
相关信息