港口桥吊用钢丝绳断丝原因分析
Fracture Wires Causes Analysis of Steel Wire Rope for Port Machine
摘 要
港口桥吊用钢丝绳在使用中发生多处断丝现象,通过化学成分分析、力学性能测试、断口分析、金相检验和显微硬度测试等方法对断丝原因进行了分析.结果表明:钢丝绳断丝的性质为疲劳断裂,断裂源位于钢丝表面的损伤或磨损处;断丝表面存在的较多磨损、挤压剥落等缺陷以及断丝显微组织中存在一定数量的铁素体共同导致了钢丝绳中钢丝的早期疲劳断裂.
断丝
疲劳
平行裂纹
steel wire rope
fracture wire
fatigue
parallel crack
Abstract
The fractured wires were found in servicing steel wire rope,which used in port machine.The fracture wires reason was analyzed by chemical composition analysis,mechanical properties test,fracture observation,metallographic examination and microhardness test,etc.The results show that fracture characteristic was fatigue.The fracture origin was in the zone of surface abrasion and squeeze-peeling.The reason caused early fracture wires involved the defects of surface abrasion,squeeze-peeling and a little ferrite in fracture wires.
中图分类号 TG729
所属栏目 失效分析
基金项目
收稿日期 2008/11/26
修改稿日期 2009/5/30
网络出版日期
作者单位点击查看
备注巴发海(1966-),男,河南郑州人,高级工程师,博士.
引用该论文: BA Fa-hai,LI Ling,LU Zhou. Fracture Wires Causes Analysis of Steel Wire Rope for Port Machine[J]. Materials for mechancial engineering, 2009, 33(12): 90～93
巴发海,李玲,陆洲. 港口桥吊用钢丝绳断丝原因分析[J]. 机械工程材料, 2009, 33(12): 90～93
被引情况:
【1】梁宇,石芷伊,梁益龙, "钒含量对不同冷速冷却后高碳珠光体钢显微组织的影响",机械工程材料 37, 19-22(2013)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】机械工程手册编辑委员会.机械工程手册[M].北京:机械工业出版社,1996.
【2】张桂林,魏福旗.钢丝中铁素体对整绳破断拉力影响研究[J].金属制品,2001,27(4):1-4.
【3】封士彩.斜井提升钢丝绳动态安全系数的探讨[J].煤矿机电,2001(6):3-5.
【4】杨旭彬.一起钢丝绳断裂事故的分析[J].机电工程技术,2004,33(12):81-82.
【5】王春晖,姚戈,尹万全.小直径钢丝绳的轴向疲劳断裂特征分析[J].金属制品,2001,27(2):35-38.
【6】姚戈,尹万全.架空索道钢丝绳断裂原因分析[J].金属制品,2002,28(1):47-50.
【7】任颂赞,陈德华,于辉.钢丝绳断裂的两类起因[J].热处理,2004,19(3):40-43.
【2】张桂林,魏福旗.钢丝中铁素体对整绳破断拉力影响研究[J].金属制品,2001,27(4):1-4.
【3】封士彩.斜井提升钢丝绳动态安全系数的探讨[J].煤矿机电,2001(6):3-5.
【4】杨旭彬.一起钢丝绳断裂事故的分析[J].机电工程技术,2004,33(12):81-82.
【5】王春晖,姚戈,尹万全.小直径钢丝绳的轴向疲劳断裂特征分析[J].金属制品,2001,27(2):35-38.
【6】姚戈,尹万全.架空索道钢丝绳断裂原因分析[J].金属制品,2002,28(1):47-50.
【7】任颂赞,陈德华,于辉.钢丝绳断裂的两类起因[J].热处理,2004,19(3):40-43.
相关信息