钨含量对钴-铝-钨合金中γ′强化相的影响
Effect of Tungsten Content on γ′ Strengthening Phase in Co-Al-W Alloy
摘 要
为了解元素钨含量对新型钴-铝-钨合金中γ′强化相的影响,用燃烧合成法制备了不同钨含量的合金,通过SEM、XRD、EPMA、DSC等方法分析了钨含量对合金中γ′强化相形貌、数量以及稳定性的影响.结果表明:钴-铝-钨合金显微组织是由富钴基体及其γ′-Co3(Al,W)强化相和少量碳化物组成;γ′-Co3(Al,W)强化相比Co3Al具有更好的稳定性,随着钨含量的增加,合金的液相线温度升高,强化相的数量也增加;当钨质量分数为26.36%时合金中γ′强化相的稳定性最好.
钴-铝-钨合金
γ′相
combustion synthesis
Co-Al-W alloy
γ′ phase
Abstract
In order to study the influence of tungsten element content on γ′ strengthening phase in Co-Al-W alloy,the alloys with different tungsten contents were prepared by combustion synthesis.The effect of tungsten content on the morphology ,amount and stablization of γ′ strengthening phase was studied by using SEM,XRD,EPMA and DSC.The results show that the microstructure of Co-Al-W alloy consisted of rich γ-Co matrix,γ′-Co3(Al,W) strengthening phase and less carbides.γ′-Co3(Al,W) strengthening phase was more stable than Co3Al phase.The liquidus temperature of the alloy increased and the amount of the strengthening phase increased as the W content inceased.The best stabilization effect of the element on the phase could obtain as the W content was 26.36wt%.
中图分类号 TG132.3
所属栏目 新材料 新工艺
基金项目
收稿日期 2009/2/6
修改稿日期 2009/8/17
网络出版日期
作者单位点击查看
备注徐仰涛(1978-),男,甘肃兰州人,讲师,博士研究生.
引用该论文: XU Yang-tao,XIA Tian-dong. Effect of Tungsten Content on γ′ Strengthening Phase in Co-Al-W Alloy[J]. Materials for mechancial engineering, 2010, 34(2): 63～66
徐仰涛,夏天东. 钨含量对钴-铝-钨合金中γ′强化相的影响[J]. 机械工程材料, 2010, 34(2): 63～66
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SIMS C T,STOLOFF N S,HAGEL W C.SuperalloysⅡ[M].New York:Wiley,1987:135-138.
【2】SUZUKI A,TRESA M,POLLOCK T M.High-temperature strength and deformation of γ/γ′ two-phase Co-A-W-base alloys[J].Acta Materialia,2008,56(6):1288-1297.
【3】TIN S,POLLOCK T M,MURPHY W.Stabilization of ther-mosolutal convective instabilities in Ni-based single-crystal superalloys:carbon additions and freckle formation[J].Metall Mater Trans A,2001,32(3):1743-1749.
【4】SATO J,OMORI T,OIKAWA K,et al.Cobalt-base high-temperature alloys[J].Science,2006,312:90-91.
【5】PING D H,CUI C Y,GU Y F,et al.Microstructure of a newly developed γ′ strengthened Co-base superalloy[J].Ultramicroscopy,2007,107:791-795.
【6】CHEN R Z,WANG L B,LI J H.Review and prospect on developments of cast superalloys[J].J Aeronaut Mater,2000,20(1):55-59.
【7】SUZUKI A,DENOLF G C,POLLOCK T M,et al.Flow stress anomalies in γ/γ’ two-phase Co-Al-W-base alloys[J].Scripta Materialia,2007,56:385-388.
【8】LI Xiang-hui,GAN Bin,FENG Qian,et al.Heat-treated microstructure of Co-Al-W ternary alloys[J].Journal of University of Science and Technology Beijing,2008,30(12):1369-1373.
【9】NAGENDER NAIDU S V,SRIRAMAMURTHY A M,RAMA RAO P.Binary alloy phase diagrams[M].Ohio:ASM International,1990:1257-1259.
【10】Handbook Committee of Practical Handbook of Engineering Materials.Practical handbook of engineering materials:wrought and cast superalloys[M].Beijing:China Standard Press,2002:765.
【11】VIATOUR P,DRAPIER J M,COUTSOURADIS D.Stabi-lity of the γ′-Co3Ti compound in simple and complex cobalt alloys[J].Cobalt,1973,3:67.
【12】OMORI J,SUTOU Y,UIKAWA K,et al.Martensitic transformation of Cu-10at%Al-9at%Ga-11at%Mn ferromagnetic alloy[J].Scripta Materialia,2005,52:1153-1156.
【13】YEH A C,TIN S.Effects of Ru on the high-temperature phase stability of Ni-base single-crystal superalloys[J].Metallurgical and Materials Transactions A,2006,37(9):262l-2631.
【14】FENG Q,NANDY T K,TIN S,et al.Solidification of high-refractory ruthenium-containing superalloys[J].Acta Mater,2003,51(1):269-284.
【2】SUZUKI A,TRESA M,POLLOCK T M.High-temperature strength and deformation of γ/γ′ two-phase Co-A-W-base alloys[J].Acta Materialia,2008,56(6):1288-1297.
【3】TIN S,POLLOCK T M,MURPHY W.Stabilization of ther-mosolutal convective instabilities in Ni-based single-crystal superalloys:carbon additions and freckle formation[J].Metall Mater Trans A,2001,32(3):1743-1749.
【4】SATO J,OMORI T,OIKAWA K,et al.Cobalt-base high-temperature alloys[J].Science,2006,312:90-91.
【5】PING D H,CUI C Y,GU Y F,et al.Microstructure of a newly developed γ′ strengthened Co-base superalloy[J].Ultramicroscopy,2007,107:791-795.
【6】CHEN R Z,WANG L B,LI J H.Review and prospect on developments of cast superalloys[J].J Aeronaut Mater,2000,20(1):55-59.
【7】SUZUKI A,DENOLF G C,POLLOCK T M,et al.Flow stress anomalies in γ/γ’ two-phase Co-Al-W-base alloys[J].Scripta Materialia,2007,56:385-388.
【8】LI Xiang-hui,GAN Bin,FENG Qian,et al.Heat-treated microstructure of Co-Al-W ternary alloys[J].Journal of University of Science and Technology Beijing,2008,30(12):1369-1373.
【9】NAGENDER NAIDU S V,SRIRAMAMURTHY A M,RAMA RAO P.Binary alloy phase diagrams[M].Ohio:ASM International,1990:1257-1259.
【10】Handbook Committee of Practical Handbook of Engineering Materials.Practical handbook of engineering materials:wrought and cast superalloys[M].Beijing:China Standard Press,2002:765.
【11】VIATOUR P,DRAPIER J M,COUTSOURADIS D.Stabi-lity of the γ′-Co3Ti compound in simple and complex cobalt alloys[J].Cobalt,1973,3:67.
【12】OMORI J,SUTOU Y,UIKAWA K,et al.Martensitic transformation of Cu-10at%Al-9at%Ga-11at%Mn ferromagnetic alloy[J].Scripta Materialia,2005,52:1153-1156.
【13】YEH A C,TIN S.Effects of Ru on the high-temperature phase stability of Ni-base single-crystal superalloys[J].Metallurgical and Materials Transactions A,2006,37(9):262l-2631.
【14】FENG Q,NANDY T K,TIN S,et al.Solidification of high-refractory ruthenium-containing superalloys[J].Acta Mater,2003,51(1):269-284.
相关信息