电瓷瓷套经三种方法机加工后的残余应力变化
Residual Stress Variation of Insulator Cylinder Machined by Three Kinds of Methods
摘 要
通过X射线衍射仪分析了一种高强度电瓷瓷套分别经金刚石锯片切割、金刚石砂轮磨削和油石抛光三种不同方法机加工后的残余应力.结果表明:机加工后电瓷瓷套表面残余应力相对较小,且均为拉应力;磨削过程产生的残余应力最大,而抛光可以有效降低电瓷瓷套表面残余应力;由于电瓷瓷套表面因为机加工产生的残余应力值往往达到其断裂强度的30%～50%,所以常会导致电瓷瓷套表面出现裂纹、崩边或豁口.
金刚石砂轮
机械加工
残余应力
insulator cylinder
diamond grinding wheel
machining
residual stress
Abstract
Residual stress of a high strength insulator cylinder machined by three kinds of methods including diamond-blade incising,diamond-wheel grinding and whetstone polishing was analyzed by using X-ray diffraction.The results show that the residual stress on the insulator cylinder surface was relatively small after machining and was tensile stress.The maximal residual stress generated during the grinding,and the polishing could decrease the stress effectively.The residual stress on the insulator cylinder surface after machining could reach 30%-50% of the rupture strength,which would result in crack,brokenedge or nick on the insulator cylinder surface.
中图分类号 TB125
所属栏目 残余应力
基金项目 高等学校学科创新引智计划资助项目(B08040);湛江师范学院重点科研资助项目(L0807)
收稿日期 2009/1/17
修改稿日期 2009/8/17
网络出版日期
作者单位点击查看
备注弓满锋(1973-),男,陕西宝鸡人,博士研究生.
引用该论文: GONG Man-feng,QIAO Sheng-ru,MEI Fang,WU Zhen-xian. Residual Stress Variation of Insulator Cylinder Machined by Three Kinds of Methods[J]. Materials for mechancial engineering, 2010, 34(2): 89～91
弓满锋,乔生儒,梅芳,吴振献. 电瓷瓷套经三种方法机加工后的残余应力变化[J]. 机械工程材料, 2010, 34(2): 89～91
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】弓满锋,梅芳,凌利兴,等.电瓷瓷套工装的开发与应用[J].工具技术,2005,39(4):66-67.
【2】祝昌军,高玲,杨海涛,等.氮化硅陶瓷磨削表面残余应力的测试与计算[J].中国有色金属学报,2002,12(增刊):41-45.
【3】田欣利,于爱兵,林彬.陶瓷磨削残余应力对表面性能的影响[J].机械科学与技术,2002,21(4):615-618.
【4】田欣利,徐燕申.陶瓷精密加工表面完整性的研究进展[J].中国机械工程,1998,9(6):63-66.
【5】何泽夏,路民旭.陶瓷材料应力腐蚀特性的测试与分析[J].硅酸盐学报,1993,21(5):15-20.
【6】ZHANG B,ZHENG X L,TOKURA H.Grinding induced damage in ceramic[J].Journal of Materials Processing Technology,2003,132(2):353-364.
【7】ROTH,WOBKER H G,MENZ C.Surface integrity and wear behavior of ground ceramics[J].Tribology Transactions,1995,38(3):714-720.
【8】谢清云,周敬恩,沈光汉.电瓷材料显微结构与力学性能的研究[J].电瓷避雷器,2000(3):12-20.
【9】周玉,武高辉.材料分析测试技术-材料X射线衍射与电子显微分析[M].哈尔滨:哈尔滨工业大学出版社,1997:96-98.
【10】邓世均.高性能陶瓷涂层[M].北京:化学工业出版社,2004:95-96.
【11】吴红兵,刘刚,柯映林,等.钛合金的已加工表面残余应力的数值模拟[J].浙江大学学报:工学版,2007,41(8):1389-1394.
【12】LYASHENKO B A,RUTHOVSKII A V,SOROKA E B,et al.On the reduction of residual stresses in plasma vacuum deposited coatings[J].Strength of Materials,2001,33(4):344-348.
【2】祝昌军,高玲,杨海涛,等.氮化硅陶瓷磨削表面残余应力的测试与计算[J].中国有色金属学报,2002,12(增刊):41-45.
【3】田欣利,于爱兵,林彬.陶瓷磨削残余应力对表面性能的影响[J].机械科学与技术,2002,21(4):615-618.
【4】田欣利,徐燕申.陶瓷精密加工表面完整性的研究进展[J].中国机械工程,1998,9(6):63-66.
【5】何泽夏,路民旭.陶瓷材料应力腐蚀特性的测试与分析[J].硅酸盐学报,1993,21(5):15-20.
【6】ZHANG B,ZHENG X L,TOKURA H.Grinding induced damage in ceramic[J].Journal of Materials Processing Technology,2003,132(2):353-364.
【7】ROTH,WOBKER H G,MENZ C.Surface integrity and wear behavior of ground ceramics[J].Tribology Transactions,1995,38(3):714-720.
【8】谢清云,周敬恩,沈光汉.电瓷材料显微结构与力学性能的研究[J].电瓷避雷器,2000(3):12-20.
【9】周玉,武高辉.材料分析测试技术-材料X射线衍射与电子显微分析[M].哈尔滨:哈尔滨工业大学出版社,1997:96-98.
【10】邓世均.高性能陶瓷涂层[M].北京:化学工业出版社,2004:95-96.
【11】吴红兵,刘刚,柯映林,等.钛合金的已加工表面残余应力的数值模拟[J].浙江大学学报:工学版,2007,41(8):1389-1394.
【12】LYASHENKO B A,RUTHOVSKII A V,SOROKA E B,et al.On the reduction of residual stresses in plasma vacuum deposited coatings[J].Strength of Materials,2001,33(4):344-348.
相关信息