Preparation and Properties of Superelastic Porous β-Phase Ti16Nb4Sn Alloy
摘 要
采用低压烧结工艺制备了多孔Ti16Nb4Sn合金,研究了烧结温度对合金的孔隙形貌、组织结构以及力学性能的影响,揭示了烧结温度对孔隙形成以及力学性能影响的机理.结果表明:1 050℃烧结制备的多孔Ti16Nb4Sn合金的孔隙率较低,闭孔较多,孔径较小(0~50 μm),呈离散状分布,组织以β相为主,含有少量α″相,合金具有超弹性:1 380℃烧结制备的多孔合金孔隙率较高,开孔度也较高,孔径分布在50~300 μm之间,呈网状分布,无明显各向异性,组织基本由β相组成,与1 050℃烧结制备的多孔合金相比,强度较高,但是超弹性较差.
Abstract
The porous Ti16Nb4Sn alloy was prepared using low pressure sintering(LPS) process.The effect of sintering temperature on the pore morphology,microstructure and mechanical properties of the alloy was studied.The mechanism of the effect was analyzed.The results show that the porous Ti16Nb4Sn alloy sintered at 1 050℃ had low porosity,many closed cells and small size pores (0-50 μm) which distributed discretely.The microstructure was composed of main β phase with few α″ phase.The alloy had superplasticity.The porous Ti16Nb4Sn alloy sintered at 1 380℃ had high porosity and open porosity,whose pore size was in the range of 50-300 μm with network-like distribution and unobvious anisotropy.The microstructure was composed of β phase.The porous Ti16Nb4Sn alloy sintered at 1 380℃ had higher strength and lower superplasticity than the alloy sintered at 1 050℃.
中图分类号 TG113:TG139
所属栏目 新材料 新工艺
基金项目 国家自然科学基金资助项目(50701019):广东省自然科学基金资助项目(2005团队项目):中国博士后科学基金资助项目(20060390199)
收稿日期 2009/3/10
修改稿日期 2009/10/31
网络出版日期
作者单位点击查看
备注李浩(1979-),男,河南西华人,博士.
引用该论文: LI Hao,GAO Yan,YUAN Bin,ZHONG Zhi-yuan. Preparation and Properties of Superelastic Porous β-Phase Ti16Nb4Sn Alloy[J]. Materials for mechancial engineering, 2010, 34(3): 41~44
李浩,高岩,袁斌,钟志源. 超弹性多孔β相Ti16Nb4Sn合金的制备及其性能[J]. 机械工程材料, 2010, 34(3): 41~44
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】KIM B S,MOONEY D J.Development of biocompatible synthetic extracellular matrices for tissue engineering[J].Trends Biotechnol,1998,16:224-230.
【2】SHABALOVSKAYA S.Laser welding of Ni-Ti shape memory alloys[C]//Proceedings of the First International Conference on Shape Memory and Superelastic Technologies.California:[s.n],1994.
【3】COSTA M,ZHUANG Z,HUANG X,et al.Molecular mechanism of nickel carcinogenesis[J].Sci Total Environ,1994,148:191-199.
【4】ITIN V,NALSENIK O,MAGEL O,et al.Corrosion behavior of NiTi based alloys in the HCl water solution[J].Metal Protection,1999,35:373-375.
【5】莱茵斯 C,皮特尔斯 M.钛与钛合金[M].陈振华,译.北京:化学工业出版社,2005.
【6】YOSHIMITSU O,YOSHIMASA I.Corrosion resistance and corrosion fatigue strength of new titanium alloys for medical implants without V and Al[J].Materials Science and Engineering A,1996,213:138-147.
【7】WANG K.The use of titanium for medical applications in the USA[J].Materials Science and Engineering A,1996,213:134-137.
【8】NAGAI Y,TOYAMA T,TANG Z,et al.Quenched-in vacancies in a b Ti-Nb-Sn alloy studied by positron lifetime spectroscopy[J].Scripta Materialis,2006,54:1751-1753.
【9】李炎,祝要民,杜三民,等.TiNbSn 合金室温组织结构的电子显微分析[J].电子显微学报,2005,24(4):288-291.
【10】HIROAKI M,SADAO W,SHUJI H.Microstructures and mechanical properties of metastable β TiNbSn alloys cold rolled and heat treated[J].Journal of Alloys and Compounds,2007,439:146-155.
【11】果世驹.粉末冶金原理[M].北京:冶金工业出版社,1998.
【12】GREEN S M,GRANT D M,KELLY N R.Powder metallurgical processing of NiTi shape memory alloy[J].Powder Metall,1997,40(1):43-47.
【13】松山芳治,三谷裕康,铃木寿.粉末冶金学[M].周安生,高一平,王 颖,等译.北京:科学出版社,1978.
【14】SEVILLA P,APARICIO C,PLANELL J A.Comparison of the mechanical properties between tantalum and nickel-titanium foams implant materials for bone ingrowth applications[J].Journal of Alloys and Compounds,2007,439(1/2):67-73.
【15】冯元桢.生物力学[M].北京:科学出版社,1983:240-250.
【16】李浩,袁斌,高岩,等.低压烧结制备多孔NiTi形状记忆合金的结构及性能[J].机械工程材料,2008,32(11):53-56.
【2】SHABALOVSKAYA S.Laser welding of Ni-Ti shape memory alloys[C]//Proceedings of the First International Conference on Shape Memory and Superelastic Technologies.California:[s.n],1994.
【3】COSTA M,ZHUANG Z,HUANG X,et al.Molecular mechanism of nickel carcinogenesis[J].Sci Total Environ,1994,148:191-199.
【4】ITIN V,NALSENIK O,MAGEL O,et al.Corrosion behavior of NiTi based alloys in the HCl water solution[J].Metal Protection,1999,35:373-375.
【5】莱茵斯 C,皮特尔斯 M.钛与钛合金[M].陈振华,译.北京:化学工业出版社,2005.
【6】YOSHIMITSU O,YOSHIMASA I.Corrosion resistance and corrosion fatigue strength of new titanium alloys for medical implants without V and Al[J].Materials Science and Engineering A,1996,213:138-147.
【7】WANG K.The use of titanium for medical applications in the USA[J].Materials Science and Engineering A,1996,213:134-137.
【8】NAGAI Y,TOYAMA T,TANG Z,et al.Quenched-in vacancies in a b Ti-Nb-Sn alloy studied by positron lifetime spectroscopy[J].Scripta Materialis,2006,54:1751-1753.
【9】李炎,祝要民,杜三民,等.TiNbSn 合金室温组织结构的电子显微分析[J].电子显微学报,2005,24(4):288-291.
【10】HIROAKI M,SADAO W,SHUJI H.Microstructures and mechanical properties of metastable β TiNbSn alloys cold rolled and heat treated[J].Journal of Alloys and Compounds,2007,439:146-155.
【11】果世驹.粉末冶金原理[M].北京:冶金工业出版社,1998.
【12】GREEN S M,GRANT D M,KELLY N R.Powder metallurgical processing of NiTi shape memory alloy[J].Powder Metall,1997,40(1):43-47.
【13】松山芳治,三谷裕康,铃木寿.粉末冶金学[M].周安生,高一平,王 颖,等译.北京:科学出版社,1978.
【14】SEVILLA P,APARICIO C,PLANELL J A.Comparison of the mechanical properties between tantalum and nickel-titanium foams implant materials for bone ingrowth applications[J].Journal of Alloys and Compounds,2007,439(1/2):67-73.
【15】冯元桢.生物力学[M].北京:科学出版社,1983:240-250.
【16】李浩,袁斌,高岩,等.低压烧结制备多孔NiTi形状记忆合金的结构及性能[J].机械工程材料,2008,32(11):53-56.
相关信息