Heat Treatment Process of High Chromium Steel Roll and Its Microstructure and Hardness
摘 要
通过SEM、EDS、XRD分析及硬度测试,研究了高铬铸钢轧辊热处理奥氏体化温度和保温时间对轧辊组织和硬度的影响规律,并确定了轧辊的热处理工艺.结果表明:随着奥氏体化温度升高和时间延长,轧辊基体中的铬含量增加,硬度先升后降;随温度升高和时间缩短,残余奥氏体增多;1 030 ℃奥氏体化保温1.5 h空冷淬火,520 ℃回火保温时间10~30 min热处理后,轧辊的组织均匀、硬化效果好,硬度达到了740~760 HV.
Abstract
By means of SEM,EDS,XRD and hardness tester,the effect of austenitizing temperature and holding time on the microstructure and hardness of high chromium steel roll was analyzed,and the heat treatment parameters of the roll were determined.The results show that with the increase of austenitizing temperature and the holding time,the hardness increased first and then decreased and with the increase of temperature and the shortening of holding time,the martensite content decreased.The roll had uniform microstructure and good hardening effect with the hardness of 740-760 HV as the roll was austenized at 1 030 ℃ for 1.5 h and air cooled,and then tempered at 520 ℃ for 10-30 min.
中图分类号 TG162.9 TG142.1
所属栏目 试验研究
基金项目
收稿日期 2009/5/8
修改稿日期 2010/2/3
网络出版日期
作者单位点击查看
备注曹燕(1963-),女,安徽马鞍山人,副教授,博士研究生.
引用该论文: CAO Yan,ZHANG Jun-tian,YIN Fu-xing,LIU Xiang-hua. Heat Treatment Process of High Chromium Steel Roll and Its Microstructure and Hardness[J]. Materials for mechancial engineering, 2010, 34(6): 13~16
曹燕,张军田,殷福星,刘相华. 高铬铸钢轧辊的热处理工艺及其组织和硬度[J]. 机械工程材料, 2010, 34(6): 13~16
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘太斗.高铬铸钢轧辊应用分析[J].太原重型机械学院学报,2004,25(9):81-84.
【2】符寒光,邢建东.高速钢轧辊制造技术[M].北京:冶金工业出版社,2007.
【3】曹燕,张军田,殷福星,等.高铬铸钢轧辊外层凝固组织研究[J].钢铁研究学报,2009,21(11):31-34.
【4】KEUN C H,LEE S,LEE H.Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls part I:microstructural analysis[J].Materials Science and Engineering A,1998,254:282-295.
【5】FU Han-guang,XIAO Qiang,LI Yan-xiang.A study of the microstructures and properties of Fe-V-W-Mo alloy modified by rare earth[J].Materials Science and Engineering A,2005,395:281-287.
【6】KANG Y J,OH J C,LEE H C.Effects of carbon and chromium additions on the wear resistance and surface roughness of cast high-speed steel rolls[J].Metallurgical and Materials Transactions A,2001,32(10):2515-2525.
【7】HUANG Zhen-hua.Comparision between 3Cr2W8V and 4Cr5MoSiV1 steels on strength and toughness[J].Heat Treatment of Metals,1988,24(7):258-263.
【2】符寒光,邢建东.高速钢轧辊制造技术[M].北京:冶金工业出版社,2007.
【3】曹燕,张军田,殷福星,等.高铬铸钢轧辊外层凝固组织研究[J].钢铁研究学报,2009,21(11):31-34.
【4】KEUN C H,LEE S,LEE H.Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls part I:microstructural analysis[J].Materials Science and Engineering A,1998,254:282-295.
【5】FU Han-guang,XIAO Qiang,LI Yan-xiang.A study of the microstructures and properties of Fe-V-W-Mo alloy modified by rare earth[J].Materials Science and Engineering A,2005,395:281-287.
【6】KANG Y J,OH J C,LEE H C.Effects of carbon and chromium additions on the wear resistance and surface roughness of cast high-speed steel rolls[J].Metallurgical and Materials Transactions A,2001,32(10):2515-2525.
【7】HUANG Zhen-hua.Comparision between 3Cr2W8V and 4Cr5MoSiV1 steels on strength and toughness[J].Heat Treatment of Metals,1988,24(7):258-263.
相关信息