新型高塑铝-镁-硅系铝合金的力学性能
Mechanical Properties of New High Plasticity Al-Mg-Si Aluminium Alloy
摘 要
在6063铝合金的基础上设计出了一种新的高塑6000系合金;采用电子万能试验机、光学显微镜和扫描电镜对铸造、挤压成型和热处理态合金的力学性能、组织特征和断口形貌进行了分析,并与6063合金进行了对比.结果表明:新的6000系合金在T6状态下抗拉强度达到282.0 MPa,伸长率达到21.7%,T4状态(48 h)的抗拉强度达到184.3 MPa,伸长率达到34.40%;与6063合金相比,T6态新合金的屈强比较小;塑性较优.
力学性能
高塑性
Al-Mg-Si alloy
mechanical property
high plasticity
Abstract
A new type of 6000 alloy with high plasticity was designed based on 6063 aluminium alloy.The mechanical properties,microstructure and fracture morphology of the alloy after casting,extrusion and heat treatment were analyzed by electronic universal testing machine,optical microscopy and scanning electron microscopy,and then compared to 6063 alloy.The results show that the tensile strength of the 6000 alloy at T6 reached 282.0 MPa and elongation reached 21.7%,while at T4 184.3 MPa and 34.40%.To compared with 6063 alloy,the alloy at T6 had low yield ratio,which indicated that the plasticity of the new type alloy was superior.
中图分类号 TG146.2
所属栏目 新材料 新工艺
基金项目 国家“863”高新技术计划资助项目(2003AA332070);长沙市科技成果产业化资金专项(K0902002-11)
收稿日期 2009/4/13
修改稿日期 2009/9/21
网络出版日期
作者单位点击查看
备注李文意(1986-),男,湖南长沙人,硕士研究生.
引用该论文: LI Wen-yi,YANG Fu-liang,MA Zheng,MENG De-chao,YIN De-yan,XIONG Luo-bao. Mechanical Properties of New High Plasticity Al-Mg-Si Aluminium Alloy[J]. Materials for mechancial engineering, 2010, 34(6): 58～60
李文意,杨伏良,马政,孟德超,尹德艳,熊落保. 新型高塑铝-镁-硅系铝合金的力学性能[J]. 机械工程材料, 2010, 34(6): 58～60
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】KELLER H.Handbook of international alloy composition[M].[S.l]:[s.n],1980.
【2】武恭,姚良均,李震夏,等.铝及铝合金材料手册[M].北京:科学出版社,1994:78.
【3】蒋建军.6063铝合金挤压型材质量影响因素及解决方法[J].铝加工,2005,161:35-39.
【4】张士林,任颂赞.简明铝合金手册[M].上海:上海科学技术文献出版社,2006:410.
【5】刘静安.Al-Mg-Si系合金的热加工工艺与可挤压性[J].铝加工,2002,25(1):1-5.
【6】ZHEN L,KANG S B.DSC analyses of the precipitation behavior of two Al-Mg-Si alloys naturally aged for different times[J].Materials Letters,1998,37(6):349-353.
【7】DORWARD R C,BOUVIER C.Rationalization of factors affecting strength,ductility and toughness of AA6061-type Al-Mg-Si-(Cu) alloys[J].Materials Science and Engineering A,1998,254:33-34.
【8】陈准.热处理制度对6013和6061合金拉伸性能的影响[J].轻合金加工技术,2001(4):25-28.
【9】张燕飞.6082T6铝合金挤压型材生产工艺[J].黑龙江冶金,2007(4):4-5.
【10】崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998:34-40.
【11】SHI H,MCLAREN J,SELLARS C M,et al.Constitutive equations for high temperature flow stress of aluminum alloys[J].Materials Science and Technical,1997,13(3):210-216.
【12】刘静安.热加工工艺对Al-Mg-Si系合金型材性能的影响[J].轻合金加工技术,2002(2):1-5.
【13】MURAYAMA M.Pre-precipitata clusters and precipitation processes in Al-Mg-Si alloys[J].Acta Mater,1999,47(5):1537-1548.
【14】束德林.金属力学性能[M].北京:机械工业出版社,1999.
【15】黄伯云,李成功,石力开,等.中国材料工程大典:有色金属材料工程[M].北京:化学工业出版社,2006:38-41.
【2】武恭,姚良均,李震夏,等.铝及铝合金材料手册[M].北京:科学出版社,1994:78.
【3】蒋建军.6063铝合金挤压型材质量影响因素及解决方法[J].铝加工,2005,161:35-39.
【4】张士林,任颂赞.简明铝合金手册[M].上海:上海科学技术文献出版社,2006:410.
【5】刘静安.Al-Mg-Si系合金的热加工工艺与可挤压性[J].铝加工,2002,25(1):1-5.
【6】ZHEN L,KANG S B.DSC analyses of the precipitation behavior of two Al-Mg-Si alloys naturally aged for different times[J].Materials Letters,1998,37(6):349-353.
【7】DORWARD R C,BOUVIER C.Rationalization of factors affecting strength,ductility and toughness of AA6061-type Al-Mg-Si-(Cu) alloys[J].Materials Science and Engineering A,1998,254:33-34.
【8】陈准.热处理制度对6013和6061合金拉伸性能的影响[J].轻合金加工技术,2001(4):25-28.
【9】张燕飞.6082T6铝合金挤压型材生产工艺[J].黑龙江冶金,2007(4):4-5.
【10】崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998:34-40.
【11】SHI H,MCLAREN J,SELLARS C M,et al.Constitutive equations for high temperature flow stress of aluminum alloys[J].Materials Science and Technical,1997,13(3):210-216.
【12】刘静安.热加工工艺对Al-Mg-Si系合金型材性能的影响[J].轻合金加工技术,2002(2):1-5.
【13】MURAYAMA M.Pre-precipitata clusters and precipitation processes in Al-Mg-Si alloys[J].Acta Mater,1999,47(5):1537-1548.
【14】束德林.金属力学性能[M].北京:机械工业出版社,1999.
【15】黄伯云,李成功,石力开,等.中国材料工程大典:有色金属材料工程[M].北京:化学工业出版社,2006:38-41.
相关信息