高温过热器炉管的爆管原因
Reason of Explosion of High Temperature Super-Heater Furnace Tube
摘 要
通过对断口、化学成分和显微组织等的分析,对某石化热电厂高炉高温过热器爆裂炉管进行了失效分析.结果表明:炉管在高温炉气的长期作用下发生内部珠光体球化和外表面渗硫导致晶间腐蚀开裂形成微裂纹是爆管的主要原因.
珠光体球化
渗硫
爆管
furnace tube
pearlite spheroidization
sulfurizing
tube explosion
Abstract
Explosion of furnace tube for blast furnace high temperature super-heater of a petrochemical thermal power plant occured.The failure reasons were analyzed by means of fracture analysis,chemical composition analysis and microstructure observation.The results indicate that inside pearlite spheroidization and surface sulfurizing,occured in the furnace tube under the consecutive effect of furnace gas with high temperature,led to intergranular corrosion cracking and micro cracks formed which was the main reason for the tube explosion.
中图分类号 TG172.9
所属栏目 失效分析
基金项目
收稿日期 2009/3/16
修改稿日期 2009/10/6
网络出版日期
作者单位点击查看
备注师红旗(1982-),男,山西长治人,硕士研究生.
引用该论文: SHI Hong-qi,WANG Yu-shun,DING Yi,MA Li-qun. Reason of Explosion of High Temperature Super-Heater Furnace Tube[J]. Materials for mechancial engineering, 2010, 34(6): 77～79
师红旗,王雨顺,丁毅,马立群. 高温过热器炉管的爆管原因[J]. 机械工程材料, 2010, 34(6): 77～79
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】束德林.工程材料力学性能[M].北京:机械工业出版社,2008.
【2】钟群鹏,赵子华.断口学[M].北京: 高等教育出版社,2006.
【3】周峥.工程材料与热处理[M].济南:山东大学出版社,2004.
【4】胡光立,谢希文.钢的热处理(原理和工艺)[M].西安:西北工业大学出版社,2004.
【2】钟群鹏,赵子华.断口学[M].北京: 高等教育出版社,2006.
【3】周峥.工程材料与热处理[M].济南:山东大学出版社,2004.
【4】胡光立,谢希文.钢的热处理(原理和工艺)[M].西安:西北工业大学出版社,2004.
相关信息