基于有限元建模的某飞机连接件螺栓头断裂分析
Failure Analysis for Bolt Head of An Aircraft Connector Based on Finite Element Modeling
摘 要
某飞机连接件的模拟试件在进行疲劳试验时发生了连接件螺栓头的早期断裂;利用ANSYS软件建立试件的三维非线性接触模型进行了应力分析,并用SEM对脱落螺栓头进行了断口分析.结果表明:由于连接件的厚度效应使得螺栓受到弯曲应力以及截面处挤压应力的共同作用,因而螺栓在高拉应力水平下发生了低周疲劳破坏;通过设计大刚度的复合型夹具使该问题获得了解决.
有限元
螺栓
应力分析
失效分析
connector
finite element
bolt
stress analysis
failure analysis
Abstract
Bolt head simulated specimens of an aircraft connector booke in the early stage during the fatigue test,the three-dimensional nonlinear contact model for the specimens was established in order to analyzed the stress by ANSYS software,while the fracture surface of the broken bolt head was studied by SEM.The results show that the bolt fracture was due to low cycle fatigue failure in high tensile stress caused by both the bending stress cause by the thickness effect and the extrusion stress at cross section.The problem was resolved by design of compound fixture with large stiffness.
中图分类号 V2
所属栏目 失效分析
基金项目 国防“十一五”预研基金资助项目(513270501);国家“863”计划资助项目(2009AA04Z406)
收稿日期 2008/11/5
修改稿日期 2010/6/6
网络出版日期
作者单位点击查看
备注刘仁宇(1984-),男,安徽临泉人,硕士研究生.
引用该论文: LIU Ren-yu,HE Yu-ting,DU Jin-qiang,SHU Wen-jun. Failure Analysis for Bolt Head of An Aircraft Connector Based on Finite Element Modeling[J]. Materials for mechancial engineering, 2010, 34(8): 79～82
刘仁宇,何宇廷,杜金强,舒文军. 基于有限元建模的某飞机连接件螺栓头断裂分析[J]. 机械工程材料, 2010, 34(8): 79～82
被引情况:
【1】姜勇,巩建鸣,汤鹏杰,余果, "精对苯二甲酸生产装置中TA2螺柱的断裂原因",机械工程材料 39, 103-106(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵美英.复合材料机械连接失效分析及强度影响因素研究[D].西安:西北工业大学,2006.
【2】何宇廷,富贵华,吴显吉,等.载荷偏心对连接件疲劳性能的影响分析[J].应用力学学报,2002,19(2):125-128.
【3】张红兵,杜建红.有限元模型中螺栓载荷施加方法的研究[J].机械设计与制造,1999,6(2):32-33.
【4】美国金属学会.金属手册第九卷上册[M].北京:机械工业出版社,1983:100-112.
【5】张栋.失效分析[M].北京:国防工业出版社,2004:94-113.
【2】何宇廷,富贵华,吴显吉,等.载荷偏心对连接件疲劳性能的影响分析[J].应用力学学报,2002,19(2):125-128.
【3】张红兵,杜建红.有限元模型中螺栓载荷施加方法的研究[J].机械设计与制造,1999,6(2):32-33.
【4】美国金属学会.金属手册第九卷上册[M].北京:机械工业出版社,1983:100-112.
【5】张栋.失效分析[M].北京:国防工业出版社,2004:94-113.
相关信息